Nickel hydride secondary battery
View Patent ↗A nickel hydride secondary battery houses an electrode group including a positive electrode and a negative electrode which are overlapped with each other via a separator with an alkaline electrolyte solution, the negative electrode includes a hydrogen absorbing alloy, a negative-electrode additive agent, a thickening agent, and a conductive material, and the negative-electrode additive agent includes at least one selected from calcium fluoride, calcium sulfide, and calcium chloride.
1. A nickel hydride secondary battery comprising:
a container; and
an electrode group housed in the container with an alkaline electrolyte solution in an air-tightly closed state, wherein
the electrode group comprises a positive electrode and a negative electrode which are overlapped with each other via a separator,
the negative electrode comprises a hydrogen absorbing alloy, a negative-electrode additive agent, a thickening agent, and a conductive material, and
the negative-electrode additive agent comprises at least one selected from calcium fluoride, calcium sulfide, and calcium chloride.
2. The nickel hydride secondary battery according to claim 1 , wherein
an additive amount of the negative-electrode additive agent is 0.1 to 1.0 parts by mass with respect to 100 parts by mass of the hydrogen absorbing alloy.
3. The nickel hydride secondary battery according to claim 1 , wherein
the thickening agent comprises at least one selected from carboxymethylcellulose, sodium polyacrylate, and hydroxypropylcellulose.
4. The nickel hydride secondary battery according to claim 1 , wherein
an additive amount of the negative-electrode additive agent is 0.1 to 1.0 parts by mass with respect to 100 parts by mass of the hydrogen absorbing alloy, and
the thickening agent comprises at least one selected from carboxymethylcellulose, sodium polyacrylate, and hydroxypropylcellulose.
5. The nickel hydride secondary battery according to claim 1 , wherein
an additive amount of the thickening agent is 0.01 to 0.1 parts by mass with respect to 100 parts by mass of the hydrogen absorbing alloy.
6. The nickel hydride secondary battery according to claim 1 , wherein
an additive amount of the negative-electrode additive agent is 0.1 to 1.0 parts by mass with respect to 100 parts by mass of the hydrogen absorbing alloy, and
an additive amount of the thickening agent is 0.01 to 0.1 parts by mass with respect to 100 parts by mass of the hydrogen absorbing alloy.
7. The nickel hydride secondary battery according to claim 1 , wherein
an additive amount of the negative-electrode additive agent is 0.1 to 1.0 parts by mass with respect to 100 parts by mass of the hydrogen absorbing alloy,
the thickening agent comprises at least one selected from carboxymethylcellulose, sodium polyacrylate, and hydroxypropylcellulose, and
an additive amount of the thickening agent is 0.01 to 0.1 parts by mass with respect to 100 parts by mass of the hydrogen absorbing alloy.
8. The nickel hydride secondary battery according to claim 1 , wherein
the hydrogen absorbing alloy has a composition represented by a general formula: Ln 1-w Mg w Ni x-y-z Al y T z , wherein Ln represents at least one element selected from a lanthanoid element, Ca, Sr, Sc, Y, Yb, Er, Ti, Zr, and Hf, T represents at least one element selected from V, Nb, Ta, Cr, Mo, Mn, Fe, Co, Ga, Zn, Sn, In, Cu, Si, P, and B, and w, x, y, and z represent 0<w<0.3, 3.00≦x≦3.80, 0.10≦y≦0.25, and 0≦z≦0.1, respectively.
9. The nickel hydride secondary battery according to claim 1 , wherein
an additive amount of the negative-electrode additive agent is 0.1 to 1.0 parts by mass with respect to 100 parts by mass of the hydrogen absorbing alloy, and
the hydrogen absorbing alloy has a composition represented by a general formula: Ln 1-w Mg w Ni x-y-z Al y T z , wherein Ln represents at least one element selected from a lanthanoid element, Ca, Sr, Sc, Y, Yb, Er, Ti, Zr, and Hf, T represents at least one element selected from V, Nb, Ta, Cr, Mo, Mn, Fe, Co, Ga, Zn, Sn, In, Cu, Si, P, and B, and w, x, y, and z represent 0<w<0.3, 3.00≦x≦3.80, 0.10≦y≦0.25, and 0≦z≦0.1, respectively.
10. The nickel hydride secondary battery according to claim 1 , wherein
an additive amount of the negative-electrode additive agent is 0.1 to 1.0 parts by mass with respect to 100 parts by mass of the hydrogen absorbing alloy,
the thickening agent comprises at least one selected from carboxymethylcellulose, sodium polyacrylate, and hydroxypropylcellulose, and
the hydrogen absorbing alloy has a composition represented by a general formula: Ln 1-w Mg w Ni x-y-z Al y T z , wherein Ln represents at least one element selected from a lanthanoid element, Ca, Sr, Sc, Y, Yb, Er, Ti, Zr, and Hf, T represents at least one element selected from V, Nb, Ta, Cr, Mo, Mn, Fe, Co, Ga, Zn, Sn, In, Cu, Si, P, and B, and w, x, y, and z represent 0<w<0.3, 3.00≦x≦3.80, 0.10≦y≦0.25, and 0≦z≦0.1, respectively.
11. The nickel hydride secondary battery according to claim 1 , wherein
an additive amount of the negative-electrode additive agent is 0.1 to 1.0 parts by mass with respect to 100 parts by mass of the hydrogen absorbing alloy,
the thickening agent comprises at least one selected from carboxymethylcellulose, sodium polyacrylate, and hydroxypropylcellulose,
an additive amount of the thickening agent is 0.01 to 0.1 parts by mass with respect to 100 parts by mass of the hydrogen absorbing alloy, and
the hydrogen absorbing alloy has a composition represented by a general formula: Ln 1-w Mg w Ni x-y-z Al y T z , wherein Ln represents at least one element selected from a lanthanoid element, Ca, Sr, Sc, Y, Yb, Er, Ti, Zr, and Hf, T represents at least one element selected from V, Nb, Ta, Cr, Mo, Mn, Fe, Co, Ga, Zn, Sn, In, Cu, Si, P, and B, and w, x, y, and z represent 0<w<0.3, 3.00≦x≦3.80, 0.10≦y≦0.25, and 0≦z≦0.1, respectively.
12. The nickel hydride secondary battery according to claim 1 , wherein
the conductive material comprises carbon black.
13. The nickel hydride secondary battery according to claim 1 , wherein
an additive amount of the negative-electrode additive agent is 0.1 to 1.0 parts by mass with respect to 100 parts by mass of the hydrogen absorbing alloy, and
the conductive material comprises carbon black.
14. The nickel hydride secondary battery according to claim 1 , wherein
an additive amount of the negative-electrode additive agent is 0.1 to 1.0 parts by mass with respect to 100 parts by mass of the hydrogen absorbing alloy,
the thickening agent comprises at least one selected from carboxymethylcellulose, sodium polyacrylate, and hydroxypropylcellulose, and
the conductive material comprises carbon black.
15. The nickel hydride secondary battery according to claim 1 , wherein
an additive amount of the negative-electrode additive agent is 0.1 to 1.0 parts by mass with respect to 100 parts by mass of the hydrogen absorbing alloy,
the thickening agent comprises at least one selected from carboxymethylcellulose, sodium polyacrylate, and hydroxypropylcellulose,
an additive amount of the thickening agent is 0.01 to 0.1 parts by mass with respect to 100 parts by mass of the hydrogen absorbing alloy, and
the conductive material comprises carbon black.
16. The nickel hydride secondary battery according to claim 1 , wherein
an additive amount of the negative-electrode additive agent is 0.1 to 1.0 parts by mass with respect to 100 parts by mass of the hydrogen absorbing alloy,
the thickening agent comprises at least one selected from carboxymethylcellulose, sodium polyacrylate, and hydroxypropylcellulose,
an additive amount of the thickening agent is 0.01 to 0.1 parts by mass with respect to 100 parts by mass of the hydrogen absorbing alloy,
the hydrogen absorbing alloy has a composition represented by a general formula: Ln 1-w Mg w Ni x-y-z Al y T z , wherein Ln represents at least one element selected from a lanthanoid element, Ca, Sr, Sc, Y, Yb, Er, Ti, Zr, and Hf, T represents at least one element selected from V, Nb, Ta, Cr, Mo, Mn, Fe, Co, Ga, Zn, Sn, In, Cu, Si, P, and B, and w, x, y, and z represent 0<w<0.3, 3.00≦x≦3.80, 0.10≦y≦0.25, and 0≦z≦0.1, respectively), and
the conductive material comprises carbon black.