POSITIVE LITHOGRAPHIC PRINTING PLATE PRECURSOR AND METHOD FOR PRODUCING THE SAME
A CTP positive working lithographic printing original plate (precursor) is capable of being imaged and then developed using a negative developing solution. This positive working lithographic printing original plate has (1) a substrate thereon (2) a lower layer containing a water-insoluble and alkali-soluble resin and a photothermal conversion material, and (3) an uppermost layer containing a water-insoluble and alkali-soluble resin. In addition, the lower layer contains (a) a polymer having a perfluoroalkyl group and/or (b) a polymer having a siloxane group in a total amount of from 3 to 10% by mass.
1 . A positive working lithographic printing original plate having (1) a substrate thereon (2) a lower layer containing a water-insoluble and alkali-soluble resin and a photothermal conversion material, and (3) an uppermost layer containing a water-insoluble and alkali-soluble resin having a carboxylic acid group or an acid anhydride group, wherein
the lower layer contains (a) a polymer having a perfluoroalkyl group and/or (b) a polymer having a siloxane group, and the total amount of the polymer (a) and/or the polymer (b) in the solid content of the lower layer is from 3 to 10% by mass.
2 . The positive working lithographic printing original plate according to claim 1 , wherein the (a) polymer having a perfluoroalkyl group further comprises a polyoxyalkylene group.
3 . The positive working lithographic printing original plate according to claim 1 , wherein the (b) polymer having a siloxane group further comprises a polyoxyalkylene group.
4 . The positive working lithographic printing original plate according to claim 1 , wherein both (a) polymer and (b) polymer are present at a ratio of the (a) polymer and the (b) polymer in the lower layer of from 15:85 to 85:15 in terms of a mass ratio.
5 . The positive working lithographic printing original plate according to claim 1 , wherein the uppermost layer is substantially free of a photothermal conversion material.
6 . The positive working lithographic printing original plate according to claim 1 , wherein the uppermost layer is soluble in an alkali developer having pH of lower than 12.
7 . A plate-making method of a positive working lithographic printing original plate comprising imagewise exposing the positive working lithographic printing original plate according to claim 1 , and developing the positive working lithographic printing original plate with a developing solution for a negative working PS plate.