Blends of linear and branched neodymium-catalyzed rubber formulations for use in golf balls
View Patent ↗The invention relates to golf ball formulations formed from blends of linear and branched polybutadienes catalyzed with neodymium that have improved properties and processing characteristics. Golf ball components may be formed from the blends to provide high coefficient of restitution.
1. A golf ball comprising a core and a cover, wherein the core is formed from a blend comprising:
a linear polybutadiene formed with a neodymium catalyst having a first polydispersity and a first Mooney viscosity of from about 30 to about 100; and
a branched polybutadiene formed with a neodymium catalyst having a second polydispersity greater than the first polydispersity and a second Mooney viscosity of from about 30 to about 75, wherein the second Mooney viscosity is less than the first Mooney viscosity.
2. The golf ball of claim 1 , wherein the linear polybutadiene has a higher Mooney Stress Relaxation than the branched polybutadiene.
3. The golf ball of claim 1 , wherein the second Mooney viscosity is of from about 35 to about 50.
4. The golf ball of claim 3 , wherein the second Mooney viscosity is about 40 to about 45.
5. The golf ball of claim 1 , wherein the branched polybutadiene has a solution viscosity to Mooney Viscosity ratio of about 3.0 to about 4.0.
6. The golf ball of claim 5 , wherein the branched polybutadiene has a solution viscosity to Mooney Viscosity ratio of about 3.6 to about 3.8.
7. The golf ball of claim 1 , wherein the linear polybutadiene has a solution viscosity to Mooney Viscosity ratio of greater than about 5.
8. The golf ball of claim 1 , wherein the solution viscosity to Mooney Viscosity ratio of the linear polybutadiene is at least about 2 times greater than the solution viscosity to Mooney Viscosity ratio of the branched polybutadiene.
9. The golf ball of claim 1 , further comprising an intermediate layer disposed between the cover and the core.
10. The golf ball of claim 1 , wherein the blend further comprises cobalt-, lithium-, titanium-, or nickel-catalyzed polybutadienes.
11. A golf ball comprising a core, a cover, and an intermediate layer disposed between the cover and the core, wherein a portion of the golf ball is formed from a blend comprising:
a linear polybutadiene formed with a neodymium catalyst having a first polydispersity and a first Mooney viscosity; and
a branched polybutadiene formed with a neodymium catalyst having a second polydispersity greater than the first polydispersity and a second Mooney viscosity less than the first Mooney viscosity, wherein the second polydispersity is greater than about 2, and wherein the second Mooney viscosity is of from about 35 to about 50.
12. The golf ball of claim 11 , wherein the linear polybutadiene has a first Mooney Stress Relaxation and the branched polybutadiene has a second Mooney Stress Relaxation, and wherein the second Mooney Stress Relaxation is less than the first Mooney Stress Relaxation.
13. The golf ball of claim 11 , wherein the first polydispersity is less than about 3.
14. The golf ball of claim 11 , wherein the first Mooney viscosity is of from about 30 to about 100.
15. The golf ball of claim 11 , wherein the core comprises a center and at least one outer core layer, and wherein at least one of the center or the outer core comprises the blend.
16. The golf ball of claim 11 , wherein the cover comprises polyurethane, polyurea, or a combination thereof.
17. A golf ball comprising a core and a cover, wherein the core comprises a blend comprising:
a linear polybutadiene formed with a neodymium catalyst having a first polydispersity and a first solution viscosity to Mooney Viscosity ratio; and
a branched polybutadiene formed with a neodymium catalyst having a second polydispersity greater than the first polydispersity and a second solution viscosity to Mooney Viscosity ratio less than the first solution viscosity to Mooney Viscosity ratio, and wherein the second solution viscosity to Mooney Viscosity ratio ranges from about 3 to about 4 and the first solution viscosity to Mooney Viscosity ratio ranges from about 5 to about 12.
18. The golf ball of claim 17 , wherein the cover comprises a thermoset material.
19. The golf ball of claim 17 , further comprising an intermediate layer formed from a thermoplastic material.
20. The golf ball of claim 17 , wherein the ratio of weight percentage of the branched polybutadiene to the linear polybutadiene is at least about 60:40.