Photocurable coating composition and its use

1. A coating process for coating a substrate comprising the step of applying onto a surface of the substrate a photocurable coating composition comprising:

a) at least one photocurable component,

b) at least one filler having an average particle size of D 50 <0.5 μm,

c) optionally one or more silanes or siloxanes,

d) at least one UV stabilizer,

e) at least one photoinitiator,

f) at least one swellable or soluble polymer selected from the group consisting of n-butyl-acrylate polymers, sec-butyl-acrylate polymers, isobutyl-acrylate polymers, tert-butyl-acrylate polymers, n-butyl-methacrylate polymers, sec-butyl-methacrylate polymers, isobutyl-methacrylate polymers, and tert-butyl-methacrylate polymers, and

g) optionally one or more solvents,

h) optionally one or more auxiliaries,

wherein the cured coating composition has a gloss value according to ASTM D2457 at 60° of less than 60,

and

further comprising the curing steps of:

(i) irradiating the coated substrate with UV-light of a wave length of less than 200 nm, and subsequently

(ii) irradiating the coated substrate obtained in step (i) with UV-light of a wave length of 200 to 440 nm.

2. The coating process for coating a substrate according to claim 1 , wherein the step of applying said photocurable composition is by a spray-coating process.

3. The coating process according to claim 1 wherein the step of applying said photocurable composition comprises the steps of:

i) providing a substrate,

ii) optionally forming a decor, a pattern or an image onto said substrate,

iii) spraying the composition onto the surface of said decor, pattern or image, and

iv) optionally drying the coated surface.

4. The coating process according to claim 3 , wherein step ii) is performed, and the formation of the decor, the pattern or the image of step ii) and the spraying of the composition of step (iii) are carried out by an ink-jet printing process.

5. Coated articles comprising a transparent topcoat obtained by the coating process of claim 1 .

6. Coated articles according to claim 5 , having a multilayer coating comprising:

a) the substrate,

b) optionally at least one primer layer on said substrate,

c) a coloured or decorative layer, and

d) the transparent topcoat layer.

7. Coated articles according to claim 5 selected from decorative elements, signs, stickers, automotive parts, eyeglasses, eyeglass frames, writing utensils, displays, flexible films and sheets, rigid films and sheets and keypads.