Low vinyl styrene-butadiene polymers and methods of making the same
View Patent ↗The invention provides a process for the continuous polymerization of a polymer comprising monomeric units derived from styrene and 1,3-butadiene, said process comprising: polymerizing the monomers in the presence of an initiator, and at least one polar agent selected from Formula 1; wherein R1 and R2 are each independently an alkyl, and preferably a C1-C4 alkyl; R3, R4, R5, R6, R7 and R8 are each independently selected from hydrogen or an alkyl, and preferably hydrogen or a C1-C4 alkyl; and wherein a 1,2-diene is added to the polymerization, and the 1,2-diene to active initiator (active for polymerization) molar ratio is from 0.1 to 1.0, preferably from 0.1 to 0.9, and more preferably from 0.1 to 0.85; and wherein the polar agent to the active initiator molar ratio is from 0.05 to 0.6, preferably from 0.1 to 0.5, more preferably from 0.15 to 0.3. The invention also provides a composition comprising a polymer comprising monomeric units derived from styrene and 1,3-butadiene, and wherein the polymer has at least the following characteristics: A) vinyl content from 12 to 40 weight percent, based on the weight of polymerized butadiene in the polymer, B) block styrene content less than 8 weight percent, based on the weight of styrene in the polymer, and C) a styrene content from 10 to 50 weight percent, based on the weight of the polymer.
1. A process for the continuous polymerization of a polymer comprising monomeric units derived from styrene and 1,3-butadiene, said process comprising:
polymerizing the monomers in the presence of an initiator, and at least one polar agent selected from Formula 1;
Formula 1,
wherein R 1 and R 2 are each independently an alkyl, and preferably a C 1 -C 4 alkyl; R 3 , R 4 , R 5 , R 6 , R 7 and R 8 are each independently selected from hydrogen or an alkyl, and preferably hydrogen or a C 1 -C 4 alkyl;
and wherein a 1,2-diene is added to the polymerization, and the 1,2-diene to active initiator molar ratio is from 0.1 to 1.0; and
wherein the polar agent to the active initiator molar ratio is from 0.05 to 0.6, wherein the polar agent comprises ditetrahydrofurylpropane.
2. The process of claim 1 , wherein the polymer has a vinyl content from 12 to 40 weight percent, based on the incorporated butadiene portion in the polymer.
3. The process of claim 1 , wherein the total monomer conversion is greater than 97.5 weight percent based on total amount of monomer feed.
4. The process of claim 1 , wherein the polymerization is run at a temperature in the range from 75°C. to 95°C.
5. The process of claim 1 , wherein the polymer has a block styrene content less than 8 weight percent, based on the incorporated styrene portion in the polymer.
6. The process of claim 1 , wherein the polymer has a styrene content from 10 to 50 weight percent, based on the total mass of the polymer.
7. The process of claim 1 , wherein the initiator comprises an organolithium compound.
8. The process of claim 1 , wherein the polar agent to the active initiator molar ratio is from 0.1 to 0.5.
9. The process of claim 1 , wherein the total monomer conversion is greater than 99 weight percent.
10. The process of claim 7 , wherein the organolithium compound comprises n-butyl lithium or sec-butyl lithium.
11. A polymer formed from the process of claim 1 .
12. A composition comprising the polymer of claim 11 .
13. An article comprising at least one component formed from the composition of claim 12 .