COMPOSITION AND PROCESS FOR MAKING FLAME LAMINATED POLYURETHANE FOAMS
A polyurethane foam forming composition, processes for making a foam from such compositions, and laminates and composites comprising foams made from such compositions. The polyurethane foams are polyether based foams that are heat bondable, such as by, for example, flame lamination, to a substrate. The foams are formed from a composition comprising a silicone based surfactant. The surfactant comprises alkyl siloxane units and units with pendant acetoxy capped polyether groups.
1 . A process for producing a flame lamination polyurethane foam slabstock comprising reacting a composition comprising:
(a) a polyether polyol containing a functionality of 2 to 6 and a number average molecular weight of about 1,000 to about 10,000 g/mole;
(b) a polyisocyanate;
(c) at least one catalyst for the production of a polyurethane foam;
(d) a flame lamination additive;
(e) a flame retardant additive;
(f) at least one blowing agent comprising water; and
(g) a silicone surfactant comprising silicone-containing polymer of the formula:
MD x D′ y M
wherein M is (CH 3 ) 3 SiO 1/2 —; D is —O 1/2 Si(CH 3 ) 2 O 1/2 —; D′ is —O 1/2 Si(CH 3 )R′O 1/2 —; x is 40 to 150; y is 5 to 40; x/y≦7; R′ is an acetoxy capped polyether; and the surfactant comprises at least two D′ units having different acetoxy capped polyethers from one another, the acetoxy capped polyether groups having 0 mole percent of the branches being ≧75% by weight ethylene oxide content; the surfactant having a target average molecular weight of about 18,000 to about 35,000 Daltons.
2 . The process of claim 1 , wherein the surfactant has a target average molecular weight of from about 20,000 to about 30,000 Daltons.
3 . The process of claim 1 , wherein the surfactant has a target average molecular weight of from about 22,000 to about 28,000 Dalton.
4 . The process of claim 1 , wherein x/y is from about 4 to about 7.
5 . The process of claim 1 , wherein the surfactant comprises three D′ units, each D′ unit having a different acetoxy capped polyethers with 0 mole percent of the branches being ≧75% by weight ethylene oxide content.
6 . A process for producing a flame lamination polyurethane foam slabstock comprising reacting a composition comprising:
(a) a polyether polyol containing a functionality of 2 to 6 and a number average molecular weight of about 1,000 to about 10,000 g/mole;
(b) a polyisocyanate;
(c) at least one catalyst for the production of a polyurethane foam;
(d) a flame lamination additive;
(e)a flame retardant additive;
(f) at least one blowing agent comprising water; and
(g) a silicone surfactant comprising silicone-containing polymer of the formula:
R—Si(CH 3 ) 2 O—(Si(CH 3 ) 2 O—) x —(SiCH 3 R 1 O—) a —(SiCH 3 R 2 O—) b —(SiCH 3 R 3 O—) c —(SiCH 3 R 4 O—) d —Si(CH 3 ) 2 —R
where R 1 , R 2 , and R 3 are polyalkylene oxide polyethers of the formula
—B—C n H 2n O—(C 2 H 4 O) e —(C 3 H 6 O) f —(C 4 H 8 O) g —Z,
R 1 has a blend average molecular weight in the range of from about 3000 to about 6000 grams/mole and ethylene oxide is from about 20 to about 60 weight percent of the alkylene oxide content of the polyether;
R 2 has a blend average molecular weight in the range of from about 800 to about 2900 grams/mole and ethylene oxide is from about 20 to about 60 weight percent of the alkylene oxide content of the polyether;
R 3 has a blend average molecular weight in the range of from about 130 to about 800 grams/mole and ethylene oxide is from 0 to about 75 weight percent of the alkylene oxide content of the polyether;
R 4 is an substituted or unsubstituted alkyl, alkaryl, or aryl group of C 1 to C 12 ;
B is derived from a moiety capable of undergoing hydrosilation;
Z is selected from the group consisting of hydrogen, C 1 -C 8 alkyl or aralkyl moieties, —C(O)Z 1 , —C(O)OZ 1 , and —C(O)NHZ 1 , where Z 1 represents mono-functional C 1 -C 8 alkyl or aryl moieties;
each R is independently selected from the group consisting of R 1 , R 2 , R 3 , and R 4 ;
x is 40 to 150;
y is 5 to 40 and equals a+b+c+d, where b or c, but not both, may be 0, d/(a+b+c)=0 to 1, and a+b>0; x/y≦7; n≧4; and e, f, and g are defined by the molecular weight required by the poly ether.
7 . The process of claim 6 , wherein x/y is ≦6.
8 . The process of claim 6 , wherein x/y is about 3 to about 7.
9 . The process of claim 6 , wherein x/y is about 4 to about 7.
10 . The process of claim 6 , wherein the surfactant comprises an a unit, a b unit, and a c unit.
11 . The process of claim 10 , wherein the a unit has a blend average molecular weight of from about 4000 to about 4500 Daltons and an ethylene oxide content of from about 40 to about 50%; the b unit has a blend average molecular weight of from about 1400 to about 1600 Daltons and an ethylene oxide content of from about 40 to about 50%, and the c unit has a blend average molecular weight of from about 400 to about 600 Daltons and an ethylene oxide content of from about 40 to 50%.
12 . The process of claims 6 , wherein the surfactant comprises an a unit, a b unit, and a d unit.
13 . The process of claim 6 , wherein the surfactant comprises an a unit, a c unit, and a d unit.
14 . The process of claim 6 , wherein the surfactant comprises an a unit and a c unit.
15 . The process of claim 14 , wherein the a unit has a blend average molecular weight of from about 4000 to about 4500 Daltons and an ethylene oxide content of from about 40 to about 50%; and the c unit has a blend average molecular weight of from about 400 to about 600 Daltons and an ethylene oxide content of from about 40 to 50%.
16 . The process of claims 6 , wherein the surfactant is present in the composition at concentration of from about 0.1 to about 5 pphp, where pphp is parts per hundred parts polyol.
17 . A process for producing a laminate or composite structure, the process comprising heat bonding a substrate to a polyurethane foam, wherein the polyurethane foam is produced by reacting a composition comprising:
(a) a polyether polyol containing a functionality of 2 to 6 and a number average molecular weight of about 1,000 to about 10,000 g/mole;
(b) a polyisocyanate;
(c) at least one catalyst for the production of a polyurethane foam;
(d) a flame lamination additive;
(e) a flame retardant additive;
(f) at least one blowing agent comprising water; and
(g) a silicone surfactant comprising silicone-containing polymer of the formula:
R—Si(CH 3 ) 2 O—(Si(CH 3 ) 2 O—) x —(SiCH 3 R 1 O—) a —(SiCH 3 R 2 O—) b —(SiCH 3 R 3 O—) c —(SiCH 3 R 4 O—) d —Si(CH 3 ) 2 —R
where R 1 , R 2 , and R 3 are polyalkylene oxide polyethers of the formula
—B—C n H 2n O—(C 2 H 4 O) e —(C 3 H 6 O) f —(C 4 H 8 O) g —Z,
R 1 has a blend average molecular weight in the range of from about 3000 to about 6000 grams/mole and ethylene oxide is from about 20 to about 60 weight percent of the alkylene oxide content of the polyether;
R 2 has a blend average molecular weight in the range of from about 800 to about 2900 grams/mole and ethylene oxide is from about 20 to about 60 weight percent of the alkylene oxide content of the polyether;
R 3 has a blend average molecular weight in the range of from about 130 to about 800 grams/mole and ethylene oxide is from 0 to about 75 weight percent of the alkylene oxide content of the polyether;
R 4 is an substituted or unsubstituted alkyl, alkaryl, or aryl group of C 1 to C 12 ;
B is derived from a moiety capable of undergoing hydrosilation;
Z is selected from the group consisting of hydrogen, C 1 -C 8 alkyl or aralkyl moieties, —C(O)Z 1 , —C(O)OZ 1 , and —C(O)NHZ 1 , where Z 1 represents mono-functional C 1 -C 8 alkyl or aryl moieties;
each R is independently selected from the group consisting of R 1 , R 2 , R 3 , and R 4 ;
x is 40 to 150;
y is 5 to 40 and equals a+b+c+d, where b or c, but not both, may be 0, d/(a+b+c)=0 to 1, and a+b>0; x/y≦7; n≧4; and e, f, and g are defined by the molecular weight required by the poly ether.
18 . The process of claim 17 , wherein x/y is about 4 to about 7.
19 . The process of claim 17 , wherein the surfactant comprises an a unit, a b unit, and a c unit.
20 . The process of claim 19 , wherein the a unit has a blend average molecular weight of from about 4000 to about 4500 Daltons and an ethylene oxide content of from about 40 to about 50%; the b unit has a blend average molecular weight of from about 1400 to about 1600 Daltons and an ethylene oxide content of from about 40 to about 50%, and the c unit has a blend average molecular weight of from about 400 to about 600 Daltons and an ethylene oxide content of from about 40 to 50%.
21 . The process of claim 17 , wherein the surfactant comprises an a unit, a b unit, and a d unit.
22 . The process of claim 17 , wherein the surfactant comprises an a unit, a c unit, and a d unit.
23 . The process of claim 17 , wherein the surfactant comprises an a unit and a c unit.
24 . The process of claim 23 , wherein the a unit has a blend average molecular weight of from about 4000 to about 4500 Daltons and an ethylene oxide content of from about 40 to about 50%; and the c unit has a blend average molecular weight of from about 400 to about 600 Daltons and an ethylene oxide content of from about 40 to 50%.
25 . The process of claim 17 , wherein the substrate is chosen from wood, paper, metal, a leather material, a fabric, a plastic, a foam, or a combination of two or more thereof
26 . The process of claim 17 , wherein the substrate is chosen from a polyvinyl chloride material.