Chemical inhibition of pitting corrosion in methanolic solutions containing an organic halide
Pitting corrosion of stainless steel occurs in solutions of organic acid, such as tartaric acid, in an electrolyte solution with methanol. However, methanolic solutions containing at least one organic halide and at least one organic hydroxyl-acid and some water provide reduced pitting corrosion of stainless steel. The organic hydroxyacid may be a hydroxy acid containing 2 to 10 carbon atoms with at least one hydroxyl group and at least one carboxylic acid group, in a non-limiting example, glycolic acid. The pH of the methanolic solution may range from about 3.5 to about 8.
1. A methanolic solution comprising:
water;
methanol;
at least one organic halide; and
at least one compound selected from the group consisting of organic hydroxyacids containing 2 to 10 carbon atoms with at least one hydroxyl group and at least one carboxylic acid group, and alkaline metal salts thereof, and amine salts thereof, and combinations thereof; where:
the methanol proportion ranges from about 5 to about 60 wt %;
the at least one organic halide proportion ranges from about 0.5 to about 70 wt %; and
the at least one compound proportion ranges from about 0.5 to about 10 wt %.
2. The methanolic solution of claim 1 where:
the water proportion ranges from about 0.01 to about 12 wt %.
3. The methanolic solution of claim 1 where the pH of the methanolic solution ranges from about 3.5 to about 8.
4. The methanolic solution of claim 1 where the at least one compound is at least one organic hydroxyacid selected from the group consisting of 2-hydroxyacetic acid (glycolic acid), 2-hydroxypropanoic acid (lactic acid), 3-hydroxypropanoic acid (hydracrylic acid), 2-hydroxybutyric acid (alpha-hydroxybutyric acid), 2-hydroxybutyric acid (beta-hydroxybutyric acid, 4-hydroxybutyric acid (gamma-hydroxybutyric acid), 2-hydroxybenzoic acid (salicylic acid), 3-hydroxybenzoic acid, 4-hydroxybenzoic acid, 3,4,5-trihydroxybenzoic acid (gallic acid), and alkaline metal salts of these organic hydroxyacids, and amine salts of these organic hydroxyacids and combinations thereof.
5. The methanolic solution of claim 1 where the at least one compound is selected from the group consisting of an ethanolamine salt of glycolic acid, a butyl amine salt of glycolic acid, a dibutylamine salt of glycolic acid, and combinations thereof.
6. The methanolic solution of claim 1 where there is an absence of ethanol.
7. The methanolic solution of claim 1 where the solution has improved pitting corrosion with respect to stainless steel when it is in contact with stainless steel as compared with an otherwise identical methanolic solution absent the at least one compound.
8. The methanolic solution of claim 1 where the only corrosion inhibitor in the methanolic solution is the at least one compound.
9. The methanolic solution of claim 1 where the at least one organic halide is selected from the group consisting of quaternary ammonium halides, organic oxazolidinium halides, and combinations thereof.
10. The methanolic solution of claim 1 where the methanol proportion ranges from about 15 wt % to about 70 wt %.
11. A methanolic solution comprising:
water;
methanol in a proportion ranging from about 5 to about 60 wt %;
at least one organic halide in a proportion ranging from about 0.5 to about 70 wt %; and
at least one organic hydroxyacid in a proportion ranging from about 0.5 to about 10 wt %, where the at least one organic hydroxyacid is selected from the group consisting of 2-hydroxyacetic acid (glycolic acid), 2-hydroxypropanoic acid (lactic acid), 3-hydroxypropanoic acid (hydracrylic acid), 2-hydroxybutyric acid (alpha-hydroxybutyric acid), 2-hydroxybutyric acid (beta-hydroxybutyric acid, 4-hydroxybutyric acid (gamma-hydroxybutyric acid), 2-hydroxybenzoic acid (salicylic acid), 3-hydroxybenzoic acid, 4-hydroxybenzoic acid, 3,4,5-trihydroxybenzoic acid (gallic acid), and alkaline metal salts of these organic hydroxyacids, and amine salts of these organic hydroxyacids and combinations thereof, and
where the pH of the methanolic solution ranges from about 3.5 to about 8.
12. The methanolic solution of claim 11 where there is an absence of ethanol.
13. The methanolic solution of claim 11 where the solution has improved pitting corrosion with respect to stainless steel when it is in contact with stainless steel as compared with an otherwise identical methanolic solution absent the at least one compound.
14. The methanolic solution of claim 11 where the only corrosion inhibitor in the methanolic solution is the at least one compound.
15. The methanolic solution of claim 11 where the at least one organic halide is selected from the group consisting of quaternary ammonium halides, organic oxazolidinium halides, and combinations thereof.
16. A methanolic solution consisting of:
water;
methanol;
at least one organic halide; and
at least one compound selected from the group consisting of organic hydroxyacid, and alkaline metal salts thereof, and amine salts thereof, and combinations thereof.
17. The methanolic solution of claim 16 where:
the water proportion ranges from about 0.01 to about 12 wt %;
the methanol proportion ranges from about 5 to about 60 wt %;
the at least one organic halide proportion ranges from about 0.5 to about 70 wt %; and
the at least one compound proportion ranges from about 0.5 to about 10 wt %.
18. The methanolic solution of claim 17 where the at least one compound is selected from the group consisting of an ethanolamine salt of glycolic acid, a butyl amine salt of glycolic acid, a dibutylamine salt of glycolic acid, and combinations thereof.