Sag resistant, formaldehyde-free coated fibrous substrate
The present invention relates to an improved formaldehyde-free coated fibrous substrate. The coating includes a crosslinked binder system which forms three dimensional networks when heat cured. After the coating is applied to the back of fibrous substrate and cured, the coating is capable of hygroscopic expansion which imparts excellent anti-sag properties. The coating is compatible with other coating systems with neutral or mild alkaline pH. The improvement being the binding system is neutralized with a volatile base so that it evaporates quickly so as not to hinder the cross-linking reaction.
1. A coating composition for application to a building panel, the coating composition comprising a blend of:
a polymeric binder comprising polyacrylic acid;
a filler;
a crosslinker that is a polyol selected from the group consisting of glycerol, dextrose, sucrose, fructose, sorbitol, and combinations thereof;
a neutralizing agent; and
a liquid carrier;
wherein the coating composition is formaldehyde-free and has a pH ranging from about 8.0 to about 8.9; and
wherein the filler and the polymeric binder are present in a weight ratio ranging from about 2:1 to about 6:1.
2. The coating composition according to claim 1 , wherein the liquid carrier comprises water.
3. The coating composition according to claim 2 , wherein the liquid carrier is present in an amount of about 45 wt. % to about 50 wt. % based on the total weight of the coating composition.
4. The coating composition according to claim 1 , wherein the coating composition has a metal ion concentration of less than 1000 ppm.
5. The coating composition according to claim 4 , the metal ion concentration is less than 500 ppm.
6. An aqueous coating composition for application to a building panel, the coating composition comprising a blend of:
a polymeric binder that is a polyacrylic acid;
a crosslinker that is a polyol selected from the group consisting of glycerol, dextrose, sucrose, fructose, sorbitol, and combinations thereof;
a neutralizing agent;
a filler;
wherein the aqueous coating composition has a pH of about 8.0; and
wherein a weight ratio of the filler to the polymeric binder is from about 2:1 to about 6:1, and the aqueous coating composition has a metal ion concentration of less than 1000 ppm.
7. The aqueous coating composition of claim 6 , wherein the aqueous coating composition is free of mica.
8. The aqueous coating composition of claim 6 , wherein the neutralizing agent comprises a volatile base.
9. The aqueous coating composition of claim 8 , wherein the volatile base is aqueous ammonia.
10. The aqueous coating composition of claim 6 , wherein the filler is selected from inorganic fillers, organic fillers and combinations thereof.
11. The aqueous coating composition of claim 10 , wherein the filler comprises inorganic fillers selected from limestone powder, clay, sand, mica, perlite, diatomaceous earth, feldspar, talc and glass beads.
12. The aqueous coating composition of claim 10 , wherein the filler comprises organic filler that includes hard plastic powders.
13. A coating composition for application to a building panel, the coating composition comprising a blend of:
a polymeric binder that is polyacrylic acid and that is at least partially neutralized with a volatile base;
a polyol crosslinker selected from the group consisting of diethanolamine, triethanolamine, glycerol, dextrose, sucrose, fructose, sorbitol, and combinations thereof;
a nonionic surfactant comprising a secondary alcohol ethoxylate;
a liquid carrier;
a filler; and
wherein the coating composition is free of mica;
wherein the coating composition is formaldehyde-free and is free of any single or multi-valence metal ions selected from sodium, potassium, and calcium;
wherein the coating composition has a pH ranging from about 8.0 to about 8.9; and
wherein a weight ratio of the filler to the polymeric binder ranges from about 2:1 to about 6:1.
14. The coating composition according to claim 13 , wherein the volatile base is aqueous ammonia.
15. The coating composition according to claim 1 , wherein the coating composition further comprises a nonionic surfactant that is a secondary alcohol ethoxylate.
16. The coating composition according to claim 6 , wherein the coating composition further comprises a nonionic surfactant that is a secondary alcohol ethoxylate.
17. The coating composition according to claim 1 , wherein the weight ratio of the filler and the polymeric binder ranges from about 2:1 to about 2.7:1.
18. The coating composition according to claim 6 , wherein the weight ratio of the filler to the polymeric binder ranges from about 2:1 to about 2.7:1.
19. The coating composition according to claim 13 , wherein the weight ratio of the filler to the polymeric binder ranges from about 2:1 to about 2.7:1.