Polyurethane and polyisocyanurate foams and methods of producing the same
The present disclosure relates to a modified polyester polyol composition useful in the formulation of polyurethane and polyisocyanurate cellular polymers for use in making foam articles with hydrocarbon blowing agents. The modified polyester polyol composition comprises the reaction product of a polyol with an EO/PO block copolymer having a weight average molecular weight from 1,000 to 20,000 g/mol and has a viscosity in the range of 100 to 10,000 centipoise, as determined at 25° C. according to the ASTM D-4878 method.
1. A foam formed by:
a) reacting an aromatic polyester polyol with an EO/PO block copolymer having a weight average molecular weight from ≥1,000 to ≤20,000 g/mol to form a homogeneous foam precursor composition with a viscosity in a range of ≥100 to ≤10,000 centipoise, as determined at 25° C. according to ASTM D-4878; and
b) contacting the homogeneous foam precursor composition of (a) with an isocyanate and a halogen-free blowing agent.
2. The foam of claim 1 , wherein the weight average molecular weight of the EO/PO block copolymer is in a range of ≥4,000 and ≤10,000 g/mol, and the homogeneous foam precursor composition viscosity is in the range of ≥1000 to ≤5,000 centipoise.
3. The foam of claim 1 , wherein the reaction between the aromatic polyester polyol and the EO/PO block copolymer is carried out in a presence of an esterification catalyst.
4. The foam of claim 1 , wherein the blowing agent is a hydrocarbon.
5. The foam of claim 1 having a weight per unit volume of at least 1.5 lb/ft 3 and an insulation R-value of greater than 6.
6. A homogeneous foam precursor for making foam with a nonhalogenated blowing agent, said homogeneous foam precursor comprising a reaction product of a polyester polyol and an EO/PO block copolymer, wherein the EO/PO block copolymer has a weight average molecular weight from ≥1,000 to ≤20,000 g/mol and the homogeneous foam precursor has a viscosity in a range of ≥100 to ≤10,000 centipoise, as determined at 25° C. according to ASTM D-4878.
7. A foam comprising a reaction product of a mixture of:
a) from 10 to 50 wt. % of the homogeneous foam precursor of claim 6 ;
b) from 30 to 80 wt. % of an organic isocyanate;
c) from 0 to 10 wt. % of a hydroxylated component other than an aromatic polyester polyol;
d) from 0 to 5 wt. % of a catalyst;
e) from 1 to 20 wt. % of a hydrocarbon as a blowing agent; and
f) from 0 to 5 wt. % of a surfactant.
8. A method for making foam comprising:
(a) reacting a polyester polyol with an EO/PO block copolymer, wherein the EO/PO block copolymer has a weight average molecular weight from ≥1,000 to ≤20,000 g/mol to form a homogeneous foam precursor having a viscosity in a range of ≥100 to ≤10,000 centipoise, as determined at 25° C. according to ASTM D-4878; and
(b) contacting the homogeneous foam precursor of (a) with an isocyanate and a non-halogenated blowing agent under foam-forming conditions.
9. The method of claim 8 , further comprising adding a catalyst during contacting the homogeneous foam precursor of step (b).