Curable composition
The present application relates to a curable composition and a use thereof. The present application can provide a curable composition having excellent physical properties such as adhesive durability as well as maintaining transparency even in a high-temperature and high-humidity environment. Such a curable composition can be usefully used for direct bonding between a filler and an optical member of a display device.
1. A curable composition comprising a curable component comprising 20 to 70 parts by weight of a reactive silicone oligomer, and a hydroxyl-containing component comprising 20 to 70 parts by weight of a non-reactive silicone oligomer having a hydroxyl group and having a hydroxyl value (OH value) of 2 to 45 mg KOH/g.
2. The curable composition according to claim 1 ,
wherein a haze is 1.0% or less, as measured with the turbidimeter ASTM D1003 standard by storing a specimen, in which the curable composition is cured to a thickness of 150 μm, at a temperature of 85° C. and a relative humidity of 85% for 1000 hours, and then leaving it at a temperature of 25° C. and a relative humidity of 50% for 1 hour.
3. The curable composition according to claim 1 ,
wherein the reactive silicone oligomer comprises a polysiloxane-based urethane (meth)acrylate.
4. The curable composition according to claim 1 ,
wherein the reactive silicone oligomer comprises a monofunctional silicone oligomer and a bifunctional silicone oligomer.
5. The curable composition according to claim 4 ,
wherein the reactive silicone oligomer further comprises a silicone oligomer having three or more functionalities.
6. The curable composition according to claim 1 ,
wherein the reactive silicone oligomer has a weight average molecular weight (Mw) of 10,000 to 100,000.
7. The curable composition according to claim 1 ,
wherein the non-reactive silicone oligomer comprises at least one oligomer of a non-reactive polysiloxane oligomer and a non-reactive polysiloxane modified urethane oligomer.
8. The curable composition according to claim 1 ,
wherein the non-reactive silicone oligomer has a weight average molecular weight (Mw) of 1,000 to 50,000.
9. The curable composition according to claim 1 ,
wherein the hydroxyl-containing component further comprises 1 to 30 parts by weight of a hydroxyl-containing reactive monomer.
10. The curable composition according to claim 9 ,
wherein the hydroxyl-containing reactive monomer is hydroxyalkyl (meth)acrylate.
11. The curable composition according to claim 1 ,
wherein the curable composition further comprises an initiator, a silane coupling agent or an antioxidant.
12. The curable composition according to claim 1 ,
wherein the curable composition has an elastic modulus at 1 Hz after curing of 10,000 Pa to 100,000 Pa.
13. The curable composition according to claim 1 ,
wherein the curable composition has a viscosity at 1 Hz and 25° C. of 1,000 cP to 10,000 cP.
14. A display device comprising at least one air gap between optical members, and comprising a cured product of the curable composition of claim 1 filling the air gap.
15. A display device comprising a display panel and a touch panel, wherein the display device further comprises a cured product of the curable composition of claim 1 attaching the display panel and the touch panel.