A method for forming a golf ball with a graphene core disclosed herein. The method includes mixing a graphene masterbatch material with a polybutadiene material to form a core mixture, wherein the graphene masterbatch material comprises graphene in an amount from 0.1 to 80.0 weight percent of the graphene masterbatch material mixed with a carrier polymer in an amount from 99.9 to 20 weight percent of the graphene masterbatch material.
1. A method for forming a golf ball with a graphene core, the method comprising:
mixing a graphene masterbatch material with a polybutadiene material to form a core mixture, wherein the graphene masterbatch material comprises graphene in an amount from 0.1 to 80.0 weight percent of the graphene masterbatch material mixed with a carrier polymer in an amount from 99.9 to 20 weight percent of the graphene masterbatch material, wherein the polybutadiene comprises 40-90 weight percent of polybutadiene, 0.4 to 2.5 weight percent graphene material, 1-30 weight percent polyisoprene, 10-50 weight percent zinc diacrylate, 1-30 weight percent zinc oxide, 1-20 weight percent zinc stearate, and 0.1-10 weight percent peroxide initiator; and
compression molding a core from the core mixture.
2. The method according to claim 1 wherein the core has a diameter ranging from 0.70 inch to 1.6 inch.
3. The method according to claim 1 further comprising forming a cover over the core.
4. The method according to claim 1 further comprising forming a mantle layer over the core.
5. The method according to claim 4 wherein the carrier polymer material is selected from the group consisting of polybutadiene, polyisoprene, polyisobutylene, EPDM, polyethylene ionomer, maleic anhydride functionalized polyethylene, styrene butadiene rubber, styrene isoprene rubber, and butyl rubber.
6. The method according to claim 1 wherein compression molding a core from the core mixture comprises compression molding a center core.
7. The method according to claim 1 wherein compression molding a core from the core mixture comprises compression molding an outer core layer over a center core comprising a polybutadiene mixture.
8. The method according to claim 1 wherein compression molding a core from the core mixture comprises compression molding a center core and an outer core over the center core, and the center core and the outer core comprise the core mixture.
9. The method according to claim 1 wherein the core mixture comprises the graphene masterbatch material in an amount ranging from 1.0 to 60 weight percent of the core mixture and the polybutadiene material in an amount ranging from 99 to 40 weight percent of the core mixture.