Chromium-enriched diffused aluminide coating
A method of applying a protective coating to an article comprises the steps of a) depositing aluminum in a surface region of an article, and b) depositing chromium is the surface region of the article subsequent to step a), whereby at least a portion of the chromium replaces at least a portion of the aluminum. Another method and an article are also disclosed.
1. An article, comprising:
a base alloy;
a corrosion-resistant coating on the base alloy, the corrosion-resistant coating containing a first region of approximately 20%-40% by weight chromium;
an aluminum diffusion zone disposed between the base alloy and the corrosion-resistant coating wherein the aluminum diffusion zone comprises less than approximately 20% chromium by weight; and
a second region immediately adjacent to the first region and extending from the first region to the aluminum diffusion zone, the second region comprising less than approximately 10% chromium by weight.
2. The article of claim 1 , wherein the first region extends between a depth of approximately 5 to approximately 60 microns (0.2 to 2.3 mils) from a surface of the coating.
3. The article of claim 1 , wherein the second region has a thickness of approximately 0.6 mils (15 microns).
4. The article of claim 1 , wherein the article is a turbine blade.
5. The article of claim 1 , wherein the article comprises external and internal surfaces and wherein the coating is applied to at least one of the external and internal surfaces.
6. The article of claim 1 , wherein the base alloy is at least one of a nickel-based superalloy and a low-chromium superalloy.
7. The article of claim 1 , wherein the corrosion-resistant coating is substantially free of alpha chromium.
8. The article of claim 1 , wherein the first region is an outer 30 to 60% of the coating thickness.
9. The article of claim 1 , wherein the aluminum diffusion zone has a portion adjacent the second region, and the portion has an aluminum concentration that is higher than a concentration of aluminum in the first and second regions.
10. The article of claim 1 , wherein aluminum concentration in the aluminum diffusion zone decreases with distance to the base alloy.