LITHIUM ION CONDUCTIVE SOLID ELECTROLYTE AND PRODUCTION METHOD FOR LITHIUM ION CONDUCTIVE SOLID ELECTROLYTE
A lithium ion conductive solid electrolyte contains a lithium ion conductive powder having a garnet-type crystal structure including at least Li, La, Zr, and O, and a lithium ion conductive polymer. The lithium ion conductive solid electrolyte can maintain its shape without use of an additional polymer different from the lithium ion conductive polymer. The lithium ion conductive solid electrolyte exhibits an activation energy of 30 kJ/mol or less at 20° C. to 80° C.
1 . A lithium ion conductive solid electrolyte which contains a lithium ion conductive powder having a garnet-type crystal structure including at least Li, La, Zr, and O, and a lithium ion conductive polymer, wherein
the lithium ion conductive solid electrolyte can maintain its shape without use of an additional polymer different from the lithium ion conductive polymer, and
exhibits an activation energy of 30 kJ/mol or less at 20° C. to 80° C.
2 . A lithium ion conductive solid electrolyte according to claim 1 , wherein
the amount by volume of the lithium ion conductive powder is 80 vol % or more relative to 100 vol % of the total amount of the lithium ion conductive powder and the lithium ion conductive polymer.
3 . A method for producing a lithium ion conductive solid electrolyte which contains a lithium ion conductive powder having a garnet-type crystal structure including at least Li, La, Zr, and O, the method comprising
a slurry preparation step of preparing a slurry containing a lithium salt, a polymer, the lithium ion conductive powder, and at least one aprotic polar solvent; and
a heating and pressurization step of heating the slurry under pressurization, thereby producing a lithium ion conductive solid electrolyte containing the lithium ion conductive powder and a lithium ion conductive polymer, wherein
the temperature of heating in the heating and pressurization step is higher than the boiling point of said at least one aprotic polar solvent and lower than the decomposition temperature of the polymer.
4 . A lithium ion conductive solid electrolyte production method according to claim 3 , wherein
the slurry contains a plurality of aprotic polar solvents.
5 . A lithium ion conductive solid electrolyte production method according to claim 4 , wherein
the temperature of heating in the heating and pressurization step is higher than the boiling point of at least one aprotic polar solvent of the plurality of aprotic polar solvents, and lower than the boiling point of at least one other aprotic polar solvent of the aprotic polar solvents.
6 . A lithium ion conductive solid electrolyte production method according to claim 5 , wherein
the pressure of pressurization in the heating and pressurization step is 100 MPa or more.
7 . A lithium ion conductive solid electrolyte production method according to claim 4 , wherein
the pressure of pressurization in the heating and pressurization step is 100 MPa or more.
8 . A lithium ion conductive solid electrolyte production method according to claim 3 , wherein
the pressure of pressurization in the heating and pressurization step is 100 MPa or more.