Reducing surface roughness of cured three-dimensional printed objects using a localized heat source
Examples of the present disclosure are directed toward methods and system for reducing surface roughness of a cured three-dimensional (3D) printed object using a localized heat source. An example method includes applying a liquid solvent to the cured 3D printed object and heating the cured 3D printed object with the liquid solvent applied thereto to a temperature below a melting point of the cured 3D printed object using a localized heat source to reduce a surface roughness of the cured 3D printed object as compared to the cured 3D printed object prior to the application of heat.
1 . A method comprising:
applying a liquid solvent to a cured three-dimensional (3D) printed object, the liquid solvent including an alcohol; and
heating the cured 3D printed object with the liquid solvent applied thereto to a temperature below a melting point of the cured 3D printed object using a localized heat source applying localized vectors of heat to reduce a surface roughness of the cured 3D printed object as compared to the cured 3D printed object prior to the application of heat.
2 . The method of claim 1 , further including forming the cured 3D printed object by forming a 3D printed object by an additive printing process with a polyamide material, and curing the 3D printed object to form the cured 3D printed object prior to applying the liquid solvent.
3 . The method of claim 1 , wherein applying the liquid solvent to the cured 3D printed object comprises at least one of:
submerging the cured 3D printed object in the liquid solvent; and
applying the liquid solvent as a layer on the cured 3D printed object.
4 . The method of claim 1 , further including removing the heat from the cured 3D printed object after between about one second to about five minutes and allowing the cured 3D printed object to transition to an ambient temperature.
5 . The method of claim 1 , further including drying the cured 3D printed object in a vacuum oven.
6 . The method of claim 1 , wherein the heating of the cured 3D printed object is to a temperature between about 100 degrees Celsius and about 300 degrees Celsius in an ambient environment, and wherein the surface roughness of the cured 3D printed object is reduced by at least three times compared to the cured 3D object prior to the application of the heat.
7 . The method of claim 1 , wherein:
the alcohol is selected from benzyl alcohol, glycerol, and propylene glycol; and
heating the cured 3D printed object with the liquid solvent applied thereto includes:
heating to the temperature below the melting point of the cured 3D printed object using the localized heat source for a period of time, and
heating to another temperature above the melting point of the cured 3D printed object using the localized heat source for a portion of the period of time.
8 . A method comprising:
forming a cured three-dimensional (3D) printed object;
applying a liquid solvent to the cured 3D printed object, the solvent including an alcohol;
heating the cured 3D printed object with the liquid solvent applied thereto to a temperature below a melting point of the cured 3D printed object using a localized heat source applying localized vectors of heat; and
after between about one second to about five minutes, removing the heat from the cured 3D printed object to reduce a surface roughness of the cured 3D printed object as compared to the cured 3D printed object prior to the application of heat.
9 . The method of claim 8 , wherein the surface roughness of the cured 3D printed object is reduced by at least ten times compared to the cured 3D object prior to the application of the heat, and the cured 3D printed object is formed from a polyamide material.
10 . The method of claim 8 , wherein the cured 3D printed object exhibits minimal change in Young's Modulus as compared to the cured 3D printed object prior to the application of the heat, and wherein for a portion of the about one second to about five minutes, applying the heat includes applying heat to another temperature that is above the melting point of the cured 3D printed object.
11 . The method of claim 8 , wherein applying the heat to the cured 3D printed object with the liquid solvent applied thereto and removing the heat causes an increase in tensile stress at maximum load and an increase in percent elongation at break as compared to the cured 3D printed object prior to the application of heat.
12 . A system comprising:
a cured three-dimensional (3D) printed object formed by an additive printing process;
a solvent source to apply a solvent in a liquid form to the cured 3D printed object, the solvent including an alcohol;
a localized heat source to apply localized vectors of heat to the cured 3D printed object; and
processor circuitry configured to cause the localized heat source to heat the cured 3D printed object with the solvent applied thereto to a temperature below a melting point of a build material forming the cured 3D printed object for between about one second to about five minutes to reduce a surface roughness of the cured 3D printed object as compared to the cured 3D printed object prior to the application of heat.
13 . The system of claim 12 , wherein the localized heat source includes a heat gun to provide the heat to the cured 3D printed object, and wherein the system further comprises an ambient environment within which the heating is performed.
14 . The system of claim 12 , wherein the cured 3D printed object has a first Young's Modulus prior to the application of heat and has about the first Young's Modulus after the application of heat, and the solvent includes a mixture including the alcohol and a second liquid, wherein the alcohol is selected from benzyl alcohol, glycerol, and propylene glycol.
15 . The system of claim 12 , further including a vacuum oven to vacuum dry the cured 3D printed object after the application of the heat.