Black ceramic sinter with low thermal expansion and high specific rigidity and process for producing the same
This invention provides a black low thermal expansion high specific rigidity ceramic sintered body having a black tone, manifesting very small thermal expansion at room temperature and abounding in rigidity and specific rigidity, and a method for the production thereof. The black low thermal expansion high specific rigidity ceramic sintered body is characterized by having a chemical composition comprising 8.0–17.2 mass % of MgO, 22.0–38.0 mass % of Al 2 O 3 , 49.5–65.0 mass % of SiO 2 , a total of 0.1–2 mass % of one or more transition elements as reduced to oxides, and 0–2.5 mass % of Li 2 O, and having the mass ratios satisfy the relationships of (SiO 2 −8×Li 2 O)/MgO≧3.0 and (SiO 2 −8×Li 2 O)/Al 2 O 3 ≧1.2. The method for the production of a black low thermal expansion high specific rigidity ceramic sintered body of this invention is characterized by forming the sintered body in an atmosphere of a non-oxidizing gas at a temperature in the range of 1200–1500° C.
1. A method for the production of a black low thermal expansion high specific rigidity ceramic sintered body, comprising:
forming the sintered body in an atmosphere of a non-oxidizing gas at a temperature in the range of 1200–1500° C.,
said black low thermal expansion high specific rigidity ceramic sintered body, comprising:
having a thermal expansion coefficient of not more than 0.6×10 −6 /° C. in absolute value at room temperature,
a modulus of elasticity (Young's modulus) of not less than 100 GPa,
a specific rigidity (Young's modulus/specific gravity) of not less than 40 GPa·cm 3 /g, and
assuming a black tone,
said black low thermal expansion high specific rigidity ceramic sintered body having a chemical composition comprising:
8.0–17.2 mass % of MgO,
22.0–38.0 mass % of Al 2 O 3 ,
49.5–65.0 mass % of SiO 2 ,
a total of 0.1–2 mass % of one or more transition elements as reduced to oxides,
0–2.5 mass % of Li 2 O, and
having the mass ratios satisfy the relationships of (SiO 2 −8×Li 2 O)/MgO≧3.0 and (SiO 2 −8×Li 2 O)/Al 2 O 3 ≧1.2.
2. A black low thermal expansion high specific rigidity ceramic sintered body, comprising:
having a thermal expansion coefficient of not more than 0.6×10 −6 /° C. in absolute value at room temperature,
a modulus of elasticity (Young's modulus) of not less than 100 GPa,
a specific rigidity (Young's modulus/specific gravity) of not less than 40 GPa·cm 3 /g, and
assuming a black tone.
3. A black low thermal expansion high specific rigidity ceramic sintered body according to claim 2 ,
wherein the total reflectivity of the sintered body is not more than 17% at a wavelength of light in the range of 200–950 nm.
4. A black low thermal expansion high specific rigidity ceramic sintered body according to claim 2 ,
wherein the apparent porosity of the sintered body is not more than 2%.
5. A black low thermal expansion high specific rigidity ceramic sintered body according to claim 2 ,
wherein not less than 80 vol. % of the crystal phase of the sintered body is a crystal phase of cordierite.
6. A black low thermal expansion high specific rigidity ceramic sintered body according to claim 2 ,
wherein the thermal expansion coefficient is not more than 0.3×10 −6 /° C. in absolute value at room temperature.
7. A black low thermal expansion high specific rigidity ceramic sintered body according to claim 2 ,
wherein the modulus of elasticity is not less than 120 GPa and the specific rigidity is not less than 50 GPa·cm 3 /g.
8. A black low thermal expansion high specific rigidity ceramic sintered body, comprising:
having a thermal expansion coefficient of not more than 0.6×10 −6 /° C. in absolute value at room temperature,
a modulus of elasticity (Young's modulus) of not less than 100 GPa,
a specific rigidity (Young's modulus/specific gravity) of not less than 40 GPa·cm 3 /g, and
assuming a black tone,
said black low thermal expansion high specific rigidity ceramic sintered body having a chemical composition comprising:
8.0–17.2 mass % of MgO,
22.0–38.0 mass % of Al 2 O 3 ,
49.5–65.0 mass % of SiO 2 ,
a total of 0.1–2 mass % of one or more transition elements as reduced to oxides,
0–2.5 mass % of Li 2 O, and
having the mass ratios satisfy the relationships of (SiO 2 −8×Li 2 O)/MgO≧3.0 and (SiO 2 −8×Li 2 O)/Al 2 O 3 ≧1.2.