Aluminide coating process
An aluminiding process that enables the cooling holes of an air-cooled component, such as a hot gas path component of a gas turbine engine, to be machined and then aluminized after all external surface coatings have been deposited. The aluminide coating is deposited using a slurry process capable of forming the aluminide coating on the component without damaging an existing ceramic coating on the component. The process involves applying an activator-free slurry containing aluminum particles that, when the component is sufficiently heated, melt and diffuse into the component surface to form the diffusion aluminide coating.
1. A process of forming a diffusion aluminide coating on a component having a ceramic coating on a first surface thereof, the process comprising the steps of:
applying a substantially uniform coating of an activator-free slurry on a second surface of the component that is not covered by the ceramic coating, the slurry consisting essentially of aluminum particles in an organic binder solution; and then
in an inert or reducing atmosphere, heating the component to melt the aluminum particles and diffuse aluminum into the second surface of the component and thereby form a diffusion aluminide coating on the second surface, the ceramic coating being substantially undamaged by the slurry during the heating step.
2. A process according to claim 1 , wherein the second surface is an internal surface defined by a hole in the component, and the first surface is an external surface intersected by the hole.
3. A process according to claim 2 , further comprising the steps of depositing the ceramic coating on the first surface of the component, and then machining the hole in the component prior to applying the slurry.
4. A process according to claim 1 , wherein the applying step comprises spraying the slurry on the second surface.
5. A process according to claim 1 , wherein the applying step comprises applying the coating on the slurry on the second surface and on the ceramic coating.
6. A process according to claim 1 , wherein the component is heated to about 960° C. to about 1090° C.
7. A process according to claim 1 , wherein the component is formed of a superalloy.
8. A process according to claim 1 , wherein the component is an air-cooled gas turbine engine component.
9. A process of forming a diffusion aluminide coating on a component having a ceramic coating on a first surface thereof, the process comprising the steps of:
applying a substantially uniform coating of an activator-free slurry on a second surface of the component that is not covered by the ceramic coating, the slurry containing aluminum particles is an inorganic binder solution; and the
in an inert or reducing atmosphere, heating the component to melt the aluminum particles and diffuse aluminum into the second surface of the component and thereby form a diffusion aluminide coating on the second surface, the ceramic coating being substantially undamaged by the slurry during the heating step, wherein the process repairs a portion of a diffusion aluminide bond coat on the second surface and exposed by a spalled region of the ceramic coating.
10. A process for forming a diffusion aluminide coating on an air-cooled superalloy component of a gas turbine engine, the process comprising the steps of:
depositing a ceramic coating on an external surface of the component;
machining holes in the component to define internal surfaces within the component, the holes intersecting the external surface of the component and at least one internal passage within the component;
applying a substantially uniform coating of an activator-free slurry to the internal surfaces of the component, the slurry containing essentially of aluminum particles in an organic binder solution;
drying the coating; and then
in an inert or reducing atmosphere, heating the component to a temperature of about 960° C. to about 1090° C. that is held for a duration sufficient to melt the aluminum particles, diffuse aluminum into the internal surfaces, and form a diffusion aluminide coating on the internal surfaces, the ceramic coating being substantially undamaged by the slurry during the heating step.
11. A process according to claim 10 , wherein the applying step comprises flowing the slurry through the internal passage and the holes to deposit the coating on the internal surfaces.
12. A process according to claim 10 , wherein the applying step comprises applying the coating on the internal surfaces and on the ceramic coating.
13. A process according to claim 10 , wherein the slurry consists of the aluminum and the inorganic binder solution.
14. A process according to claim 1 , wherein the slurry consits essentially of the aluminum particles, the inorganic binder solution, silicon and chromia.
15. A process according to claim 1 , wherein the slurry consists of the aluminum particles, the inorganic binder solution, silicon and chromia.
16. A process according to claim 2 , wherein the applying step comprises flowing the slurry through the hole in the component to deposit the coating.