Encapsulated long life electroluminescent phosphor
A process for making an electroluminescent phosphor having a given emission spectra A, comprises the steps of manufacturing a beginning electroluminescent phosphor having an emission spectra B, different than A. A coating is applied to the phosphor having the emission spectra B to increase the resistance of the phosphor to the deleterious effects of moisture and change the emission spectra of the phosphor to emission spectra A. The application of the coating includes the steps of reacting a coating precursor with a mixture of oxygen and ozone.
1. A process for making an ZnS:Cu electroluminescent phosphor having a given emission spectra A that has a CIE y value between 0.230 and about 0.200, comprising the steps of: manufacturing a beginning electroluminescent phosphor having an emission spectra B that has a CIE y value of about 0.250, applying a coating to said phosphor having said emission spectra B to change the emission spectra of said phosphor to emission spectra A, said application of said coating including the steps of reacting trimethylaluminum with a mixture of oxygen and ozone.
2. The process of claim 1 wherein the emission spectra A and the emission spectra B have a CIE x value of about 0.160.
3. The process of claim 1 wherein the phosphor contains from 0.032% to 0.039% copper by weight.