Thermoplastic resin composition, molding made of the thermoplastic resin composition and process of manufacturing the molding
View Patent ↗A molding made of a thermoplastic resin composition that comprises a thermoplastic resin component and an elastomer component partly blending in with each other is continuously heated at a temperature higher than 120° C. but lower than a melting point of each of the two components for at least one hour so as thereby to cause the thermoplastic resin component to separate and precipitate in the elastomer component.
1. A thermoplastic resin composition having a sea-island-lake structure comprising:
a matrix of a thermoplastic resin component as a sea; and
a noncross-linked elastomer component forming islands as domains in said sea;
wherein said thermoplastic resin component precipitates to form lakes as domains in said islands.
2. A thermoplastic resin composition as defined in claim 1 , wherein said thermoplastic resin component comprises a polypropylene resin.
3. A thermoplastic resin composition as defined in claim 1 , wherein, when providing a photomicrograph of said thermoplastic resin composition dyed with a ruthenium tetroxide solution by use of a transmission electron microscope, said photomicrograph shows substantially equal contrast between said “sea” and said “lake”.
4. A thermoplastic resin composition as defined in claim 1 , wherein, when analyzing said thermoplastic resin composition in spectroscopic analysis of electron energy loss said “sea” and said “lake” are substantially equal in spectral distribution pattern representing bonded states of carbon.
5. A thermoplastic resin composition as defined in claim 1 , wherein said thermoplastic resin composition further comprises an additive component incompatible with said thermoplastic resin component and compatible with said elastomer component, said additive component forming lakes as domains in said islands.
6. A molding made of a thermoplastic resin composition having a sea-island-lake structure, said thermoplastic composition comprising a matrix of a thermoplastic resin component as a sea and a noncross-linked elastomer component forming islands as domains in said sea, wherein said thermoplastic resin component precipitates to form lakes as domains in said islands.
7. A molding as defined in claim 6 , wherein said thermoplastic resin component comprises a polypropylene resin.
8. A molding as defined in claim 6 , wherein, when providing a photomicrograph of said thermoplastic resin composition dyed with a ruthenium tetroxide solution by use of a transmission electron microscope, said photomicrograph shows substantially equal contrast between said “sea” and said “lake”.
9. A molding as defined in claim 6 , wherein, when analyzing said thermoplastic resin composition in spectroscopic analysis of electron energy loss, said “sea” and said “lake” are substantially equal in spectral distribution pattern representing bonded states of carbon.
10. A molding as defined in claim 6 , wherein said thermoplastic resin composition further comprises an additive component incompatible with said thermoplastic resin component and compatible with said elastomer component, said additive component forming lakes as domains in said islands.
11. A process of manufacturing a molding from a thermoplastic resin composition having a sea-island-lake structure comprising a matrix of a thermoplastic resin component as a sea and a noncross-linked elastomer component forming islands as domains in said sea, wherein said thermoplastic resin component precipitates to form lakes as domains in said islands, said process comprising the step of continuously heating said molding at a heating temperature above approximately 120° C. but below a melting temperature of each of said thermoplastic resin component and said elastomer component for at least one hour so as thereby to cause said thermoplastic resin composition to separate and precipitate in said islands of said elastomer composition.
12. A process as defined in claim 11 , wherein said thermoplastic resin composition further comprises an additive component incompatible with said thermoplastic resin component and compatible with said elastomer component and forms lakes as domains in said islands, and said heating temperature is above approximately 120° C. but below a melting temperature of each of said thermoplastic resin component, said elastomer component and said additive component.
13. A process as defined in claim 12 , wherein said thermoplastic resin component, said elastomer component and said additive component comprise a polypropylene resin, a styrene elastomer and a polystyrene resin, respectively.
14. A process as defined in claim 11 , wherein said thermoplastic resin component comprises a polypropylene resin.
15. A process as defined in claim 11 , wherein, when providing a photomicrograph of said thermoplastic resin composition dyed with a ruthenium tetroxide solution by use of a transmission electron microscope, said photomicrograph shows substantially equal contrast between said “sea” and said “lake”.
16. A process as defined in claim 11 , wherein, when analyzing said thermoplastic resin composition in spectroscopic analysis of electron energy loss, said “sea” and said “lake” are substantially equal in spectral distribution pattern representing bonded states of carbon.