Coating composition
View Patent ↗A Chromium VI-free coating composition comprises a binder and a corrosion inhibitor in a solvent, wherein the binder comprises a silicate and an organic titanate, and the corrosion inhibitor comprises aluminium particles and zinc particles preferably flakes. The composition may also comprise an anti-corrosion additive which comprises a metal phosphate, a lubricant which comprises a polyolefin wax, and/or a thickener. The coating composition is useful for coating substrates such as nuts, bolts and other fasteners, door, bonnet and boot lock parts, hinges, door stoppers, window guides, seat belt components, brake rotors and drums, and other transportation industry related parts.
1. A coating composition which comprises a binder and a corrosion inhibitor in a solvent, wherein the binder consists essentially of a silicate and an organic titanate, and the corrosion inhibitor comprises aluminium particles and zinc particles.
2. A composition according to claim 1 wherein the binder comprises 20 to 60% by weight silicate and 40 to 80% by weight organic titanate to a total of 100% by weight.
3. A composition according to claim 1 wherein the corrosion inhibitor comprises 80 to 97% by weight of zinc particles and 3 to 20% by weight of aluminium particles to a total of 100% by weight.
4. A composition according to claim 1 which further includes an anti-corrosion additive which comprises a metal phosphate.
5. A composition according to claim 1 which further includes a lubricant which is selected from the group of a hydrocarbon or polytetraethylene wax.
6. A composition according to claim 1 which further includes a thickener.
7. A composition according to claim 1 having a solid content which comprises 50 to 80% by weight of corrosion inhibitor, 9 to 18% by weight of binder, 0 to 33% by weight of a metal phosphate, 0 to 8% by weight of a lubricant, and 0 to 4% by weight of a thickener.
8. A substrate having a coating which is formed from 1,2 or 3 coating layer(s) of a composition according to claim 1 .
9. A substrate having a coating in accordance with claim 8 , wherein there is provided a further 1 to 3 layers of a metal particle free top-coat comprising a silicate and an organic titanate in a solvent.
10. A substrate in accordance with claim 8 wherein the substrate is selected from nuts, bolts and other fasteners, door, bonnet and boot lock parts, hinges, door stoppers, window guides, seat belt components, brake rotors and drums, and other transportation industry related parts.
11. A composition according to claim 1 which further includes a lubricant which is selected from the group of a hydrocarbon or polytetrafluoroethylene wax.
12. A substrate having a coating which is formed from 1, 2 or 3 layer(s) of a composition which comprises a binder and a corrosion inhibitor in a solvent, wherein the binder comprises a silicate and an organic titanate, and the corrosion inhibitor comprises aluminum particles and zinc particles, and a further 1, 2 or 3 coating layers of an additional coating composition which comprises 20–25% by weight of a lubricant mixture of phenolic resin, epoxy resin, vinyl butyral resin, and polytetrafluoroethylene, and 70–75% by weight of a solvent mixture of methyl ethyl ketone, methyl isobutyl ketone, and cyclohexanone.
13. A substrate in accordance with claim 12 wherein the substrate is selected from nuts, bolts and other fasteners, door, bonnet and boot lock parts, hinges, door stoppers, window guides, seat belt components, brake rotors and drums, and other transportation industry related parts.