Corrosion-resistant coatings and methods of manufacturing the same
A clear protective coating including a composition having a formula SiO x C y H z , wherein x=0.8-1.5, y=1.0-2.0, and z=1.6-3.7 is provided. The coating may be formed by plasma-enhanced chemical vapor deposition. The coating typically coats a substrate, and more particularly, a metal substrate. In a preferred embodiment, the coating coats an architectural hardware article, thereby providing corrosion and abrasion protection for the architectural hardware article.
1. An article comprising: a substrate having an optically-transparent coating on at least a portion thereof, the coating comprising a composition of formula SiO x C y H z , wherein x=about 0.8-1.5, y=about 1.0-2.0, and z=about 1.6-3.7, wherein the coating has a thickness greater than 5 μm, the article is an architectural hardware item chosen from a door handle, door lever, door grip, appliance handle, hand rail, an escutcheon, a knob, trim, decorative trim hardware and combinations thereof, and the substrate comprises metal.
2. The article of claim 1 , wherein the coating is about 5 μm to about 17 μm thick.
3. The article of claim 1 , wherein the coating protects the article from corrosion for a minimum of 200 hours when exposed to an ASTM-B117 salt-fog test.
4. The article of claim 1 , wherein the substrate is metal plated.
5. The article of claim 1 , wherein the coating is applied to the substrate using plasma-enhanced chemical vapor deposition.
6. An article comprising: a substrate having an optically-transparent coating on at least a portion thereof, the coating comprising a composition of formula SiO x C y H z , wherein x=about 0.8-1.5, y=about 1.0-2.0, and z=about 1.6-3.7, wherein the coating has a thickness greater than 5 μm, and the substrate comprises at least one of brass, zinc, aluminum, steel, and chrome.
7. An article comprising: a substrate having a coating deposited thereon using physical vapor deposition (PVD), the PVD coating comprising at least one of titanium, titanium nitride, zirconium, zirconium nitride, chromium, chromium nitride, titanium-aluminum nitride, copper, copper nitride, aluminum, nickel, tin, brass, and combinations thereof, the PVD coating having an optically-transparent coating on at least a portion thereof, the optically-transparent coating comprising a composition of formula SiO x C y H z , wherein x=about 0.8-1.5, y=about 1.0-2.0, and z=about 1.6-3.7, and wherein the coating has a thickness greater than 5 μm.
8. The article of claim 7 , wherein the coating is greater than 5 μm to about 17 μm thick.
9. The article of claim 7 , wherein the optically-transparent coating protects the article from corrosion for a minimum of 200 hours when exposed to an ASTM-B117 salt-fog test.
10. The article of claim 7 , wherein the article is an architectural hardware item.
11. The article of claim 10 , wherein the architectural hardware item is chosen from a door handle, door lever, door grip, appliance handle, hand rail, an escutcheon, knob trim, decorative trim hardware and combinations thereof.
12. The article of claim 11 , wherein the optically-transparent coating is applied using plasma-enhanced chemical vapor deposition.
13. The article of claim 7 , wherein the metal substrate comprises at least one of zinc, aluminum, brass, chrome, and steel.