Reclaimed magnesium desulfurization agent

1. A desulfurization agent for removing sulfur from molten iron including magnesium, a gas-producing compound and a calcium compound, at least a majority of said magnesium in the form of reclaimed magnesium, said reclaimed magnesium at least partially formed from ground particles of a briquette or puck of magnesium scrap, said ground particles having an average particle size of about 18–100 Mesh, said ground particles including 1–15% liquid, said liquid including said gas-producing compound, said gas-producing compound including lubrication fluid, cutting fluid, water or mixtures thereof, said calcium compound including calcium oxide, calcium carbide, calcium carbonate, calcium chloride, calcium cyanamide, calcium iodide, calcium nitrate or mixtures thereof, said reclaimed magnesium including pure magnesium, a solid magnesium compound, a magnesium alloy or mixtures thereof, said gas-producing compound constituting about 0.1–10 weight percent of said desulfurization agent, said calcium compound constituting at least about 1 weight percent of said desulfurization agent, said magnesium constituting at least about 5 weight percent of said desulfurization agent.

2. A method for forming a desulfurization agent comprising:

a) obtaining a magnesium material, at least a portion of said magnesium material being reclaimed magnesium;

b) forming said reclaimed magnesium into a compressed briquette or puck by removing fluid from magnesium chips, magnesium turnings or mixtures thereof and compressing the magnesium chips, magnesium turnings or mixtures thereof into said compressed briquette or puck having a density of at least about 80 lbs/ft 3 and a fluid content of about 1–10 weight percent, said liquid including a gas-producing compound, said gas producing compound including lubrication fluid, cutting fluid, water or mixtures thereof;

c) grinding said magnesium material to form particles having an average particle size of about 18–100 Mesh; and,

d) mixing a calcium compound with said magnesium material, said calcium compound at least partially coated with said liquid in said particles of briquette or puck as said calcium compound is mixed with said magnesium material.

3. The method as defined in claim 2 , including the step of at least partially co-grinding said magnesium material and said calcium compound to form a desulfurization agent having an average particle size of about 18–100 Mesh.

4. The method as defined in claim 2 , wherein said calcium compound constitutes at least about 1 weight percent of said desulfurization agent, said calcium compound including calcium oxide, calcium carbide, calcium carbonate, calcium chloride, calcium cyanamide, calcium iodide, calcium nitrate or mixtures thereof.

5. The method as defined in claim 3 , wherein said calcium compound constitutes at least about 1 weight percent of said desulfurization agent, said calcium compound including calcium oxide, calcium carbide, calcium carbonate, calcium chloride, calcium cyanamide, calcium iodide, calcium nitrate or mixtures thereof.

6. The method as defined in claim 2 , wherein said desulfurization agent includes about 0.1–10 weight percent gas-producing compound, at least about 1 weight percent calcium compound, and at least about 5 weight percent magnesium material.

7. The method as defined in claim 5 , wherein said desulfurization agent includes about 0.1–10 weight percent gas-producing compound, at least about 1 weight percent calcium compound, and at least about 5 weight percent magnesium material.