Process for making, and use of, anionic clay materials
Anionic clay compounds such as hydrotalcite-like compounds can be made by a process wherein a non-hydrotalcite-like compound (or a hydrotalcite-like compound) are heat treated and then hydrated to form hydrotalcite-like compounds having properties (e.g., increased hardness and/or density) that differ from those of hydrotalcite-like compounds made by prior art methods wherein non-hydrotalcite-like compounds (or hydrotalcite-like compounds) are not similarly heat treated and hydrated to form such hydrotalcite-like compounds.
1. A hydrotalcite like compound having an XRD pattern which has 2 theta peak positions that reasonably resemble those found in ICDD card 35-965 and one or more metallic oxidants selected from the group consisting of cerium, vanadium, cobalt, copper, platinum, palladium, rhodium, iridium, molybdenum, tungsten, chromium, nickel, manganese, iron, ytterbium and uranium made by a process comprising:
(i) preparing a reaction mixture comprising a magnesium containing compound and an aluminum containing compound;
(ii) heat aging the reaction mixture of step (i) at a temperature less than 250° C.;
(iii) heat treating the product of step (ii) at a temperature between about 300° C. and 850° C.; and
(iv) hydrating the product of step (iii) to produce the hydrotalcite like compound.
2. The hydrotalcite like compound of claim 1 , wherein step (iv) comprises hydrating the product of step (iii) with water to produce the hydrotalcite like compound.
3. The hydrotalcite like compound of claim 1 , wherein the molar ratio of Mg:Al is from 2:1 to 5:1 in the hydrotalcite like compound.
4. A method for decreasing SO x emissions from an FCC unit comprising adding the hydrotalcite like compound of claim 1 to the FCC unit to reduce the SO x emissions.
5. The composition of claim 1 , wherein the one or more metallic oxidants do not affect the crystal structure of the hydrotalcite like compound.
6. A hydrotalcite like compound having an XRD pattern which has 2 theta peak positions that reasonably resemble those found in ICDD card 35-965 and one or more metallic oxidants selected from the group consisting of cerium, vanadium, cobalt, copper, platinum, palladium, rhodium, iridium, molybdenum, tungsten, chromium, nickel, manganese, iron, ytterbium and uranium made by a process comprising:
(i) preparing a reaction mixture comprising a magnesium containing compound and an aluminum containing compound;
(ii) heat treating the product of step (i) at a temperature between about 300° C. and 850° C.; and
(iii) hydrating the product of step (ii) to produce the hydrotalcite like compound.
7. The hydrotalcite like compound of claim 6 , wherein step (iii) comprises hydrating the product of step (ii) with water to produce the hydrotalcite like compound.
8. The anionic clay of claim 6 , wherein the molar ratio of Mg:Al is
from 2:1 to 5:1 in the hydrotalcite like compound.
9. A method for decreasing SO x emissions from an FCC unit comprising adding the anionic clay of claim 6 to the FCC unit to reduce the SO x emissions.
10. The composition of claim 6 , wherein the one or more metallic oxidants do not affect the crystal structure of the hydrotalcite like compound.
11. A hydrotalcite like compound having an XRD pattern which has 2 theta peak positions that reasonably resemble those found in ICDD card 35-965 and one or more metallic oxidants selected from the group consisting of cerium, vanadium, cobalt, copper, platinum, palladium, rhodium, iridium, molybdenum, tungsten, chromium, nickel, manganese, iron, ytterbium and uranium made by a process comprising:
(i) providing a first hydrotalcite like compound;
(ii) heat treating the first hydrotalcite like compound at a temperature up to about 850° C.; and
(iii) hydrating the product of step (ii) to form the hydrotalcite like compound having an XRD pattern which has 2 theta peak positions that are nearly identical to those found in ICDD card 35-965.
12. The hydrotalcite like compound of claim 11 , wherein the hydrotalcite like compound is at least 10% harder and/or at least 10% denser than the hydrotalcite like compound of step (i).
13. The hydrotalcite like compound of claim 11 , wherein the process comprises heat treating the hydrotalcite like compound at a temperature from about 300° C. to about 850° C.
14. The hydrotalcite like compound of claim 11 , wherein step (iii) comprises hydrating the product of step (ii) with water to produce the hydrotalcite like compound.
15. A method for decreasing SO x emissions from an FCC unit comprising adding the hydrotalcite like compound of claim 11 to the FCC unit to reduce the SO x emissions.
16. A shaped hydrotalcite-like compound comprising a magnesium-containing compound and an aluminum-containing compound and one or more metallic oxidants selected from the group consisting of cerium, vanadium, cobalt, copper, platinum, palladium, rhodium, iridium, molybdenum, tungsten, chromium, nickel, manganese, iron, ytterbium and uranium, wherein the molar ratio of Mg:Al is from 2:1 to 5:1, wherein the shaped hydrotalcite-like compound is in the form of a microspheroidal particle, a pellet or an extrudate, wherein the hydrotalcite like compound has an XRD pattern which has 2 theta peak positions that reasonably resemble those found in ICDD card 35-965.
17. The shaped hydrotalcite-like compound of claim 16 , wherein the hydrotalcite like compound has the formula: (Mg m Al n (OH) 2m+2n )OH n/a a − .bH 2 O, wherein a is 1, 2 or 3; b is between 0 and 10; and m and n are selected so that the ratio of m/n is about 1 to about 10.
18. The shaped hydrotalcite-like compound of claim 16 , wherein the hydrotalcite like compound has the formula: (Mg m Al n (OH) 2m+2n )A n/a a − .bH 2 O, wherein A is CO 3 , NO 3 , SO 4 , Cl, OH, Cr, I, SiO 3, HPO 3 , MnO 4 , HGaO 3 , HVO 4 , ClO 4 BO 3 or a mixture of two or more thereof; a is 1, 2 or 3; b is between 0 and 10; and m and n are selected so that the ratio of m/n is about 1 to about 10.
19. A binder or matrix material consisting of a shaped hydrotalcite like compound having an XRD pattern which has 2 theta peak positions that reasonably resemble those found in ICDD card 35-965 and one or more metallic oxidants selected from the group consisting of cerium, vanadium, cobalt, copper, platinum, palladium, rhodium, iridium, molybdenum, tungsten, chromium, nickel, manganese, iron, ytterbium and uranium.
20. The binder or matrix material of claim 19 in the form of a microspheroidal particle, a pellet or an extrudate.
21. A method for decreasing SO x emissions from an FCC unit comprising adding a hydrotalcite like compound that has an XRD pattern which has 2 theta peak positions that reasonably resemble those found in ICDD card 35-965 and one or more metallic oxidants selected from the group consisting of cerium, vanadium, cobalt, copper, platinum, palladium, rhodium, iridium, molybdenum, tungsten, chromium, nickel, manganese, iron, ytterbium and uranium to the FCC unit to reduce the SO x emissions.
22. A method for sorbing a chemical species in an FCC unit comprising adding a hydrotalcite like compound that has an XRD pattern which has 2 theta peak positions that reasonably resemble those found in ICDD card 35-965 and one or more metallic oxidants selected from the group consisting of cerium, vanadium, cobalt, copper, platinum, palladium, rhodium, iridium, molybdenum, tungsten, chromium, nickel, manganese, iron, ytterbium and uranium to the FCC unit to sorb the chemical species.
23. A method for catalyzing a reaction in an FCC unit comprising adding a hydrotalcite like compound that has an XRD pattern which has 2 theta peak positions that reasonably resemble those found in ICDD card 35-965 and one or more metallic oxidants selected from the group consisting of cerium, vanadium, cobalt, copper, platinum, palladium, rhodium, iridium, molybdenum, tungsten, chromium, nickel, manganese, iron, ytterbium and uranium to the FCC unit to catalyze the reaction.
24. The product of claim 1 , further comprising heat treating the hydrotalcite like compound of step (iv) at a temperature between about 300° C. and 850° C.
25. The method product of claim 6 , further comprising heat treating the hydrotalcite like compound of step (iii) at a temperature between about 300° C. and 850° C.
26. The product of claim 11 , further comprising heat treating the hydrotalcite like compound of step (iii) at a temperature between about 300° C. and 850° C.