Inorganic particles as a dental material and a method of producing the same
View Patent ↗Amorphous inorganic particles as a dental material includes silica and inorganic oxide(s) other than silica and has high x-ray impermeability. The inorganic particles as a dental material includes silica with the content in the range from 70 to 98 weight % and oxide(s) of one or more elements selected from the group of Zr, Ti, La, Ba, Sr, Hf, Y, Zn, AL, and B, wherein 5 to 70 weight % of the silica is originated from an acidic silicic acid solution and 30 to 95 weight % of the silica is originated from a sol of silica. The inorganic particles as a dental material have an average particle diameter in the range from 1 to 10 μm, specific surface area in the range from 50 to 350 m 2 /g, pore volume in the range from 0.05 to 0.5 ml/g, amorphous crystallinity as observed by x-ray diffraction, and the refractive index in the range from 1.47 to 1.60.
1. Inorganic particles as a dental material comprising silica in a range from 70 to 98 weight % and at least one oxide of at least one element selected from the group consisting of Zr, Ti, La, Ba, Sr, Hf, Y, Zn, AL, and B, wherein 5 to 70 weight % of the silica is originated from an acidic silicic acid solution and 30 to 95 weight % of the silica is originated from a sol of silica, said inorganic particles having an average particle diameter in a range from 1 to 10 μm, specific surface area in a range from 50 to 350 m 3 /g, pore volume in a range from 0.05 to 0.5 ml/g and amorphous crystallinity as observed by x-ray diffraction.
2. The inorganic particles as a dental material according to claim 1 , wherein a refractive index is in a range from 1.47 to 1.60.
3. A method of manufacturing inorganic particles as a dental material with a silica content in a range from 70 to 98 weight % comprising the steps of:
mixing an acidic silicic acid solution, a sol of silica, and an aqueous solution of metal salt of one or more elements selected from the group consisting of Zr, Ti, La, Ba, Sr, Hf, Y, Zn, AL, and B;
spray-drying a mixture slurry; and
heating obtained particles.
4. The method of manufacturing inorganic particles as a dental material according to claim 3 , wherein the mixing is performed so that a relation between SiO 2 (S Z ) in the sol of silica and SiO 2 (S A ) in the acidic silicic acid solution satisfies an equation of S A /(S A +S Z )=0.05 to 0.70.