Coating composition having improved release properties and the process for making the same
A protective coating composition and a method for coating a metal substrate are provided. The composition and method are particularly suitable for coating can ends. The coating composition includes a film-forming polymer that includes an epoxy-based resin, a lubricant system, and a solvent or water component or mixture of solvent and water. The lubricant system includes a first surface modifier that reduces the coefficient of friction and a second surface modifier that reduces the abrasion of the cured coating.
1. An exterior beverage container can end coating composition which comprises:
from about 10% to about 50% solids based on the weight of the coating composition, the solids comprising:
a) an epoxy-based resin;
b) from about 0.1% to about 20% by weight of a lubricant system which comprises:
carnauba wax; and
polyethylene; and
c) a solvent selected from an organic material, water, or a mixture of an organic material and water,
wherein the coefficient of friction (COF) of the coating composition when dried is 0.07 or less.
2. The coating composition of claim 1 , wherein the coating composition comprises;
from about 0.1% to about 16% by weight of the carnauba wax; and
from about 0.1% to about 16% by weight of the polyethylene.
3. The coating composition of claim 1 , further comprising, by weight, from about 0.1% to about 40% of a cross-linker.
4. The coating composition of claim 3 , wherein the cross-linker is selected from the group of melamine-formaldehyde, urea-formaldehyde, phenol-formaldehyde, benzoguanamine-formaldehyde resins, or blends thereof, which are optionally partially or fully etherified with alcohols.
5. The coating composition of claim 1 , further comprising, by weight, from about 2% to about 10% of a cross-linker.
6. The coating composition of claim 1 , wherein the solvent of organic material is selected from xylene, benzene, ethyl benzene, toluene, alkoxy alkanols alcohols with or without alkyl ethers of ethylene or propylene glycol, ethylene glycol monobutyl ether, ethylene glycol ethyl ether, or diethylene glycol monobutyl ether arid the solvent is present in an amount of at least about 50% by weight, based on the liquid coating composition.
7. The coating composition of claim 1 , wherein the water is present as a solvent in an amount from about 30% to about 45%.
8. The coating composition of claim 1 , wherein the water is present as a solvent along with water-soluble materials selected from butanol, propanol, or ethylene glycol monoethyl ether.
9. The coating composition of claim 1 wherein the lubricant system is present in a dispersion having an average particle size distribution that ranges from about 0.5 to about 5 microns.
10. The coating composition of claim 1 , wherein the lubricant system further comprises at least one of a surfactant and a dispersing polymer.
11. The coating composition of claim 10 , wherein the surfactant or dispersing polymer or mixtures thereof are selected from anionic and nonionic surfactants and the epoxy-based resin used as a dispersing polymer.
12. The coating composition of claim 10 , wherein the surfactant or dispersing polymer or mixtures thereof are present in an amount from about 0.5% to about 30% by weight, based on the total solids in the coating composition.
13. The coating composition of claim 1 , wherein the epoxy-based resin is selected from epoxy-acrylic resins, epoxy-polyester resins, or epoxy-phosphate resins.
14. The coating composition of claim 13 , wherein the epoxy acrylic resin is in an aqueous dispersion.
15. The coating composition of claim 1 , further comprising, by weight up to about 50% of a cross-linker.
16. The coating composition of claim 15 wherein the cross-linker also functions as the dispersing polymer.
17. The coating composition of claim 1 without polyvinylchloride.
18. The coating composition of claim 1 , wherein the polyethylene is a polyethylene wax.
19. The coating composition of claim 1 , wherein the polyethylene is a polyethylene has a molecular weight of less than about 20,000.
20. The coating composition of claim 1 , wherein the carnauba wax and the polyethylene are present as a carnauba wax and polyethylene blend dispersion.
21. The coating composition of claim 1 , wherein the coefficient of friction of the coating when dried is in the range of from about 0.05 to 0.07.
22. A method for coating an exterior beverage container metal substrate, which comprises:
applying a coating composition to the metal substrate;
heating the metal substrate and coating composition until the coating composition is cured to produce a cured coating film having a film weight that ranges from about 1 mg/in 2 to about 8 mg/in 2 ;
wherein the cured coating film comprises, by weight, based on the total solids in the coating composition, from about 50% to about 99.5% epoxy-based resin;
from at least about 0.1% of carnauba wax; and
from at least about 0.1% of polyethylene; and
wherein the cured coating film has a coefficient of friction that is 0.07 or less.
23. A metal substrate with properties such as those of aluminum, iron, steel or copper having at least one surface with a cured film of a coating composition coated by the method of claim 22 as ends or shells for easy open cans.
24. An exterior beverage container can end coating composition, which comprises:
from about 10% to about 50% solids based on the weight of the coating composition, the solids comprising:
a) an epoxy-based resin;
b) from about 0.1% to about 20% by weight of a lubricant system present as a dispersion having an average particle size distribution ranging from about 0.5 to about 5 microns , which comprises:
carnauba wax; and
a polyethylene surface modifier for abrasion resistance; and
c) up to about 50% by weight of a cross-linker, and a solvent selected from an organic material, water, or a mixture of an organic material and water, wherein the coefficient of friction (COF) of the coating composition when dried is less than about 0.05.