Copolymers of cyclic esters and cyclic formals
View Patent ↗Disclosed are copolymers of cyclic esters, e.g., caprolactone, and cyclic formals of substituted or unsubstituted diols, e.g., 1,3-dioxepane. The copolymers can provide a low melting temperature rendering them liquids at room temperature. Elastomeric polyurethanes prepared from such copolymers can exhibit a low Tg transition and good resistance to hydrolysis and oxidation. The copolymers are particularly useful for elastomers, coatings, adhesives, inks or binders requiring low temperature flexibility and good resistance to hydrolysis and oxidation.
1. A copolymer polymerized from monomers including,
(i) a cyclic ester of at least a five membered ring; and
(ii) a cyclic formal of a substituted or unsubstituted diol having at least 3 atoms between the hydroxyl groups of the diol;
wherein the cyclic ester and the cyclic formal monomers comprise at least 50 wt. % of the total monomers based on the total weight of the copolymer; wherein the copolymer is polymerized in the presence of a polymerization initiator selected from the group consisting of ethylene glycol; 1,4-butanediol; 1,6 hexanediol; 1,3-propanediol; 2,2-dimethyl-1,3-propanediol; diethylene glycol; triethylene glycol; glycerol; 2-ethyl-2-hydroxymethyl-1,3-propanediol; 2-methyl-2-hydroxymethyl-1.3-propanediol; 2-methyl-2-ethyl-1,3-propanediol; 2-ethyl-2-butyl-1,3-propanediol; 1,3-bis(hydroxymethylcyclohexane); 1,4-bis(hydroxymethylcyclohexane); and mixtures thereof.
2. The copolymer of claim 1 wherein the cyclic ester is a 5 to 9 membered ring.
3. The copolymer of claim 1 wherein the cyclic ester is a lactone selected from the group consisting of γ-butyrolactone, δ-valerolactone, ε-caprolactone and derivatives thereof.
4. The copolymer of claim 3 wherein the lactone is ε-caprolactone.
5. The copolymer of claim 1 wherein the cyclic formal is 1,3-dioxepane.
6. The copolymer of claim 1 which is polymerized from a sum of at least 75 wt. % of the cyclic aster and the cyclic formal based on the total weight of the copolymer.
7. The copolymer of claim 1 which is polymerized from monomers including one or more monomers other than the cyclic ester and the cyclic formal.
8. The copolymer of claim 7 which is polymerized from less than 50 wt. % of said one or more monomers other than the cyclic ester and the cyclic formal, based on the total weight of the copolymer.
9. The copolymer of claim 7 which is polymerized from less than 10 wt. % of said one or more monomers other than the cyclic ester and the cyclic formal, based on the total weight of the copolymer.
10. The copolymer of claim 7 which is polymerized from less than 1 wt. % of said one or more monomers other than the cyclic ester and the cyclic formal, based on the total weight of the copolymer.
11. The copolymer of claim 7 wherein the said one or more monomers other than the cyclic ester and the cyclic formal are one or more of 1,3-dioxepan-2-one, 5,5-dimethyl-1,3-dioxan-2-one, 1,3-dioxan-2-one, ethylene carbonate, propylene carbonate, 1-4-dioxane-2-one, 1,4-dioxepan-2-one, 1,5-dioxepan-2-one, 1,6-dioxepan-2-one, 3,6-dimethyl-1,4-dioxane-2,5-dione (lactide), 1,4-dioxane-2,5-dione (glycolide), and 1,3,5-trioxane.
12. The copolymer of claim 1 wherein the cyclic ester is caprolactone and the cyclic formal is 1,3-dioxepane.
13. The copolymer of claim 12 where the weight ratio of caprolactone to 1,3-dioxepane is from about 0.05:1 to 20:1.
14. The copolymer of claim 12 where the weight ratio of caprolactone to 1,3-dioxepane is from about 0.3:1 to 3:1.
15. The copolymer of claim 1 having a melting point below about 25° C.
16. An article made from the copolymer of claim 1 .
17. A composition comprising the copolymer of claim 1 and a carbodiimide additive.
18. An article made from the composition of claim 17 .
19. A polyurethane comprising the reaction product of an organic isocyanate and the copolymer of claim 1 .
20. A polyurethane comprising the reaction product of:
(a) an organic isocyanate; and
(b) a copolymer polymerized from monomers including,
(i) a cyclic ester of at least a five membered ring; and
(ii) a cyclic formal of a substituted or unsubstituted diol having at least 3 atoms between the hydroxyl groups of the diol;
wherein the cyclic ester and the cyclic formal monomers comprise at least 50 wt. % of the total monomers based on the total weight of the copolymer.
21. A process for the manufacture of a copolymer, comprising polymerizing, in the presence of a catalyst, monomers including:
(i) a cyclic ester of at least a five membered ring; and
(ii) a cyclic formal of a substituted or unsubstituted diol having at least 3 carbon atoms between the hydroxyl groups of the diol; wherein the cyclic ester and cyclic formal monomers comprise at least 50 wt. % of the total monomers based on the total weight of the copolymer; wherein the copolymer is polymerized in the presence of a polymerization initiator selected from the group consisting of ethylene glycol; 1,4-butanediol; 1,6 hexanediol; 1,3-propanediol; 2,2-dimethyl-1,3-propanediol; diethylene glycol; triethylene glycol; glycerol; 2-ethyl-2-hydroxymethyl-1,3-propanediol; 2-methyl-2-hydroxymethyl-1,3-propanediol; 2-methyl-2-ethyl-1,3-propanediol; 2-ethyl-2-butyl-1,3-propanediol; 1,3-bis(hydroxymethylcyclohexane); 1,4-bis(hydroxymethylcyclohexane); and mixtures thereof.
22. The process of claim 21 wherein the catalyst is selected from the group consisting of triflic acid, trifluoroacetic acid, methanesulfonic acid, fluorosulfonic acid, toluenesulfonic acid, phosphoric acid, anhydrous sulfuric acid, anhydrous hydrochloric acid, triflic anhydride and mixtures thereof.
23. The process of claim 22 wherein the catalyst is triflic acid.
24. The process of claim 21 further comprising adding a carbodiimide additive following the polymerization.
25. A composition comprising:
(a) a copolymer polymerized from monomers including,
(i) a cyclic ester of at least a five membered ring; and
(ii) a cyclic formal of a substituted or unsubstituted diol having at least 3 atoms between the hydroxyl groups of the diol;
wherein the cyclic ester and the cyclic formal monomers comprise at least 50 wt. % of the total monomers based on the total weight of the copolymer; and
(b) a carbodiimide additive.
26. An article made from the composition of claim 25 .
27. A process for the manufacture of a copolymer, comprising polymerizing, in the presence of a catalyst, monomers including:
(i) a cyclic ester of at least a five membered ring; and
(ii) a cyclic formal of a substituted or unsubstituted diol having at least 3 carbon atoms between the hydroxyl groups of the diol; wherein the cyclic ester and cyclic formal monomers comprise at least 50 wt. % of the total monomers based on the total weight of the copolymer; and
wherein the catalyst is selected from the group consisting of triflic acid, trifluoroacetic acid, methanesulfonic acid, fluorosulfonic acid, toluenesulfonic acid, phosphoric acid, anhydrous sulfuric acid, anhydrous hydrochloric acid, triflic anhydride and mixtures thereof.
28. The process of claim 27 further comprising adding a carbodiimide additive following the polymerization.