The invention concerns a process for extracting hemicellulose from fiber, such as corn fiber. The process comprises agitating at least fiber, caustic and optional added water at a moisture content from about 10% to about 60% at high speeds in a highly fluidized state. The process substantially instantaneously extracts the hemicellulose from the fiber. Heat may be applied in the process to extract and dry the hemicellulose substantially simultaneously.
1. A process for extracting hemicellulose from fiber comprising the step of agitating fiber, caustic and, optionally, added water at a moisture content from about 10% by weight to about 60% by weight of the fiber, caustic and optional added water at speeds of about 300 rpm to about 2,000 rpm.
2. The process of claim 1 wherein the moisture content is about 15% by weight to about 50% by weight of the fiber, caustic and optional added water.
3. The process of claim 1 wherein the moisture content is about 20% by weight to about 40% by weight of the fiber, caustic and optional added water.
4. The process of claim 1 wherein the caustic is in amount of about 10% by dry weight of the fiber to about 40% by dry weight of the fiber.
5. The process of claim 4 wherein the amount of caustic is about 10% by dry weight of the fiber to about 25% by dry weight of the fiber.
6. The process of claim 1 wherein the agitation is for about 10 seconds to about 10 minutes.
7. The process of claim 1 comprising the further step of heating during agitation up to a temperature of about 180° F.
8. The process of claim 7 wherein the temperature is from about 90° F. to about 150° F.
9. The process of claim 1 wherein the fiber is selected from the group consisting of corn, tapioca, wheat, sago, bagasse and combinations thereof.
10. The process of claim 1 wherein the caustic comprises an alkali metal hydroxide.
11. The process of claim 10 wherein the alkali metal hydroxide is selected from the group consisting of sodium hydroxide, potassium hydroxide, calcium hydroxide and combinations thereof.
12. The process of claim 1 comprising the further step of adding materials selected from the group consisting of enzymes, acids, oxidants and combinations thereof to the fiber, caustic and optional added water during or before the agitation to reduce the viscosity or color of the extracted hemicellulose.
13. The process of claim 1 conducted in a means for mixing.
14. The process of claim 13 wherein the means for mixing is selected from the group consisting of mixers, blenders, reactors, extruders, size reducers, mills and combinations thereof.
15. The process of claim 14 wherein the reactor is a thermal reactor.
16. The process of claim 1 comprising the further step of adding materials selected from the group consisting of acids, bases and combinations thereof to the fiber, caustic and optional added water during the agitation to reduce pH.