Methods of making ceramic particles
Method for making ceramic particles. Embodiments of ceramic particles made according to the present invention can be are particularly useful as abrasive particles.
1. A method for making ceramic particles, the method comprising:
providing first and second generally opposed surfaces;
providing a mold comprising a plurality of at least one of particle openings or cavities;
introducing a melt to at least a portion of the plurality of at least one of the particle openings or cavities of the mold, the melt comprising at least 35 percent by weight Al 2 O 3 , based on the total weight of the melt, and a first metal oxide other than Al 2 O 3 wherein the melt contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , based on the total weight of the melt;
passing the mold and the melt between the first and second generally opposed surface under pressure such that the melt in the at least one of the particle openings or cavities is under pressure; and
at least partially cooling the melt in the at least one of the particle openings or cavities to provide ceramic particles comprising glass, the glass comprising at least 35 percent by weight Al 2 O 3 , based on the total weight of the glass, and a first metal oxide other than Al 2 O 3 , wherein the glass contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , based on the total weight of the glass.
2. The method according to claim 1 , wherein the first and second generally opposed surfaces are exterior surfaces of first and second rollers.
3. The method according to claim 2 , wherein the mold is an endless sheet.
4. The method according to claim 3 , wherein the mold rotates about an axis.
5. The method according to claim 2 , wherein the at least one of the particle openings or cavities have at least one shape selected from the group consisting of triangles, squares, rectangles, cubes, circles, cylinders, half-cylinders, stars, crescents, semi-circles, and pyramids.
6. The method according to claim 2 , further comprising heat-treating the ceramic particles to convert at least a portion of the glass to glass-ceramic particles.
7. The method according to claim 6 , wherein the melt comprises at least 35 percent by weight Al 2 O 3 , based on the total weight of the melt, a first metal oxide other than Al 2 O 3 , and a second, different metal oxide other than Al 2 O 3 , wherein the melt contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , based on the total weight of the melt; and wherein the glass comprises at least 35 percent by weight Al 2 O 3 , based on the total weight of the glass, a first metal oxide other than Al 2 O 3 , and a second, different metal oxide other than Al 2 O 3 , wherein the glass contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , based on the total weight of the glass.
8. The method according to claim 7 , wherein the melt further comprises third, different metal oxide other than Al 2 O 3 and the first metal oxide, and wherein the glass further comprises third, different metal oxide other than Al 2 O 3 and the first metal oxide.
9. The method according to claim 2 , further comprising heat-treating the glass particles to convert at least a portion of the glass to glass-ceramic abrasive particles.
10. The method according to claim 9 , wherein the glass-ceramic abrasive particles have an average hardness of at least 17 GPa.
11. The method according to claim 9 , wherein the glass-ceramic abrasive particles have an average hardness of at least 18 GPa.
12. The method according to claim 9 , wherein the glass-ceramic abrasive particles have an average hardness of at least 19 GPa.
13. The method according to claim 9 , wherein the glass-ceramic abrasive particles have an average hardness of at least 20 GPa.
14. The method according to claim 9 , wherein at least a portion of the heating is conducted using a rotary kiln.
15. The method according to claim 9 , further comprises grading the glass-ceramic abrasive particles to provide a plurality of particles having a specified nominal grade.
16. The method according to claim 9 , further comprises grading the glass particles to be heat-treated to provide a plurality of particles having a specified nominal grade.
17. The method according to claim 9 , further comprising incorporating at least a portion of the glass-ceramic abrasive particles into an abrasive article.
18. The method according to claim 17 , wherein the abrasive article is a bonded abrasive article, a non-woven abrasive article, or a coated abrasive article.
19. The method according to claim 9 , wherein the melt comprises at least 35 percent by weight Al 2 O 3 , based on the total weight of the melt, a first metal oxide other than Al 2 O 3 , and a second, different metal oxide other than Al 2 O 3 , wherein the melt contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , based on the total weight of the melt; and wherein the glass comprises at least 35 percent by weight Al 2 O 3 , based on the total weight of the glass, a first metal oxide other than Al 2 O 3 , and a second, different metal oxide other than Al 2 O 3 , wherein the glass contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , based on the total weight of the glass.
20. The method according to claim 19 , wherein the melt further comprises third, different metal oxide other than Al 2 O 3 and the first metal oxide, and wherein the glass further comprises third, different metal oxide other than Al 2 O 3 and the first metal oxide.
21. The method according to claim 1 , wherein the mold is an endless sheet.
22. The method according to claim 21 , wherein the mold rotates about an axis.
23. The method according to claim 1 , wherein the melt comprises at least 35 percent by weight Al 2 O 3 , based on the total weight of the melt, a first metal oxide other than Al 2 O 3 , and a second, different metal oxide other than Al 2 O 3 , wherein the melt contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , based on the total weight of the melt; and wherein the glass comprises at least 35 percent by weight Al 2 O 3 , based on the total weight of the glass, a first metal oxide other than Al 2 O 3 , and a second, different metal oxide other than Al 2 O 3 , wherein the glass contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , based on the total weight of the glass.
24. The method according to claim 23 , wherein the melt further comprises third, different metal oxide other than Al 2 O 3 and the first metal oxide, and wherein the glass further comprises third, different metal oxide other than Al 2 O 3 and the first metal oxide.
25. A method for making ceramic particles, the method comprising:
providing a roll comprising a plurality of particle cavities;
introducing a melt to at least a portion of the plurality of particle cavities, the melt comprising at least 35 percent by weight Al 2 O 3 , based on the total weight of the melt, and a first metal oxide other than Al 2 O 3 , wherein the melt contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , based on the total weight of the melt;
and
at least partially cooling the melt in the particle cavities to provide ceramic particles comprising glass, the glass comprising at least 35 percent by weight Al 2 O 3 , based on the total weight of the glass, and a first metal oxide other than Al 2 O 3 , wherein the glass contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TcO 2 , and V 2 O 5 , based on the total weight of the glass;
and
contacting a surface to the melt in the cavities such that the melt in the cavities is under pressure.
26. The method according to claim 25 , wherein the particle cavities have at least one shape selected from the group consisting of triangles, squares, rectangles, cubes, circles, cylinders, half-cylinders, stars, crescents, semi-circles, and pyramids.
27. The method according to claim 25 , further comprising heat-treating the glass particles to convert at least a portion of the glass to glass-ceramic particles.
28. The method according to claim 27 , wherein the melt comprises at least 35 percent by weight Al 2 O 3 , based on the total weight of the melt, a first metal oxide other than Al 2 O 3 , and a second, different metal oxide other than Al 2 O 3 , wherein the melt contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , based on the total weight of the melt; and wherein the glass comprises at least 35 percent by weight Al 2 O 3 , based on the total weight of the glass, a first metal oxide other than Al 2 O 3 , and a second, different metal oxide other than Al 2 O 3 , wherein the glass contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , based on the total weight of the glass.
29. The method according to claim 28 , wherein the melt further comprises third, different metal oxide other than Al 2 O 3 and the first metal oxide, and wherein the glass further comprises third, different metal oxide other than Al 2 O 3 and the first metal oxide.
30. The method according to claim 25 , further comprising heat-treating the glass particles to convert at least a portion of the glass to glass-ceramic abrasive particles.
31. The method according to claim 30 , wherein the glass-ceramic abrasive particles have an average hardness of at least 17 GPa.
32. The method according to claim 30 , wherein the glass-ceramic abrasive particles have an average hardness of at least 18 GPa.
33. The method according to claim 30 , wherein the glass-ceramic abrasive particles have an average hardness of at least 19 GPa.
34. The method according to claim 30 , wherein the glass-ceramic abrasive particles have an average hardness of at least 20 GPa.
35. The method according to claim 30 , wherein at least a portion of the heating is conducted using rotary kiln.
36. The method according to claim 30 , further comprises grading the glass-ceramic abrasive particles to provide a plurality of particles having a specified nominal grade.
37. The method according to claim 30 , further comprises grading the glass particles to be heat-treated to provide a plurality of particles having a specified nominal grade.
38. The method according to claim 30 , further comprising incorporating at least a portion of the glass-ceramic abrasive particles into an abrasive article.
39. The method according to claim 38 , wherein the abrasive article is a bonded abrasive article, a non-woven abrasive article, or a coated abrasive article.
40. The method according to claim 30 , wherein the melt comprises at least 35 percent by weight Al 2 O 3 , based on the total weight of the melt, a first metal oxide other than Al 2 O 3 , and a second, different metal oxide other than Al 2 O 3 , wherein the melt contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TcO 2 , and V 2 O 5 , based on the total weight of the melt; and wherein the glass comprises at least 35 percent by weight Al 2 O 3 , based on the total weight of the glass, a first metal oxide other than Al 2 O 3 , and a second, different metal oxide other than Al 2 O 3 , wherein the glass contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , based on the total weight of the glass.
41. The method according to claim 40 , wherein the melt further comprises third, different metal oxide other than Al 2 O 3 and the first metal oxide, and wherein the glass further comprises third, different metal oxide other than Al 2 O 3 and the first metal oxide.
42. A method for making ceramic particles, the method comprising:
providing first and second generally opposed surfaces;
providing a mold comprising a plurality of at least one of particle openings or cavities;
introducing a melt to at least a portion of the plurality of at least one of the particle openings or cavities of the mold,
passing the mold and the melt between the first and second generally opposed surface under pressure such that the melt in the at least one of particle the openings or cavities is under pressure;
at least partially cooling the melt in the at least one of the particle openings or cavities to provide ceramic particles comprising glass; and
heat-treating the ceramic particles to convert at least a portion of the glass to glass-ceramic particles, wherein the glass-ceramic has an average hardness of at least 13 GPa.
43. The method according to claim 42 , wherein the first and second generally opposed surfaces are exterior surfaces of first and second rollers.
44. The method according to claim 42 , wherein the glass-ceramic has an average hardness of at least 15 GPa.
45. The method according to claim 44 , wherein the at least one of particle openings or cavities have at least one shape selected from the group consisting of triangles, squares, rectangles, cubes, circles, cylinders, half-cylinders, stars, crescents, semi-circles, and pyramids.
46. The method according to claim 44 , further comprises grading the glass-ceramic particles to provide a plurality of particles having a specified nominal grade.
47. The method according to claim 44 , further comprises grading the glass particles to be heat-treated to provide a plurality of particles having a specified nominal grade.
48. The method according to claim 44 , further comprising incorporating at least a portion of the glass-ceramic particles into an abrasive article.
49. The method according to claim 48 , wherein the abrasive article is a bonded abrasive article, a non-woven abrasive article, or a coated abrasive article.
50. The method according to claim 42 , wherein the glass-ceramic has an average hardness of at least 17 GPa.
51. The method according to claim 50 , wherein the melt comprises at least 35 percent by weight Al 2 O 3 , based on the total weight of the melt, a first metal oxide other than Al 2 O 3 , and a second, different metal oxide other than Al 2 O 3 , wherein the melt contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , based on the total weight of the melt; and wherein the glass comprises at least 35 percent by weight Al 2 O 3 , based on the total weight of the glass, a first metal oxide other than Al 2 O 3 , and a second, different metal oxide other than Al 2 O 3 , wherein the glass contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , based on the total weight of the glass.
52. The method according to claim 51 , wherein the melt further comprises third, different metal oxide other than Al 2 O 3 and the first metal oxide, and wherein the glass further comprises third, different metal oxide other than Al 2 O 3 and the first metal oxide.
53. The method according to claim 42 , wherein the glass-ceramic has an average hardness of at least 18 GPa.
54. The method according to claim 42 , wherein the glass-ceramic has an average hardness of at least 19 GPa.
55. The method according to claim 42 , wherein the glass-ceramic has an average hardness of at least 20 GPa.
56. A method for making ceramic particles, the method comprising:
providing a roll comprising a plurality of particle cavities;
introducing a melt to at least a portion of the plurality of particle cavities;
at least partially cooling the melt in the particle cavities to provide ceramic particles comprising glass; and
heat-treating the ceramic particles to convert at least a portion of the glass to glass-ceramic particles, wherein the glass-ceramic has an average hardness of at least 13 GPa.
57. The method according to claim 56 further comprising contacting a surface to the melt in the cavities such that the melt in the cavities is under pressure.
58. The method according to claim 56 , wherein the glass-ceramic has an average hardness of at least 15 GPa.
59. The method according to claim 56 , wherein the particle cavities have at least one shape selected from the group consisting of triangles, squares, rectangles, cubes, circles, cylinders, half-cylinders, stars, crescents, semi-circles, and pyramids.
60. The method according to claim 56 , further comprises grading the glass-ceramic particles to provide a plurality of particles having a specified nominal grade.
61. The method according to claim 56 , further comprises grading the glass particles to be heat-treated to provide a plurality of particles having a specified nominal grade.
62. The method according to claim 56 , further comprising incorporating at least a portion of the glass-ceramic particles into an abrasive article.
63. The method according to claim 62 , wherein the abrasive article is a bonded abrasive article, a non-woven abrasive article, or a coated abrasive article.
64. The method according to claim 56 , wherein the glass-ceramic has an average hardness of at least 17 GPa.
65. The method according to claim 64 , wherein the melt comprises at least 35 percent by weight Al 2 O 3 , based on the total weight of the melt, a first metal oxide other than Al 2 O 3 , and a second, different metal oxide other than Al 2 O 3 , wherein the melt contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , based on the total weight of the melt; and wherein the glass comprises at least 35 percent by weight Al 2 O 3 , based on the total weight of the glass, a first metal oxide other than Al 2 O 3 , and a second, different metal oxide other than Al 2 O 3 , wherein the glass contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , based on the total weight of the glass.
66. The method according to claim 65 , wherein the melt further comprises third, different metal oxide other than Al 2 O 3 and the first metal oxide, and wherein the glass further comprises third, different metal oxide other than Al 2 O 3 and the first metal oxide.
67. The method according to claim 56 , wherein the glass-ceramic has an average hardness of at least 18 GPa.
68. The method according to claim 56 , wherein the glass-ceramic has an average hardness of at least 19 GPa.
69. The method according to claim 56 , wherein the glass-ceramic has an average hardness of at least 20 GPa.
70. A method for making ceramic particles, the method comprising:
providing a roll comprising a plurality of particle openings, wherein the roller has an inner major surface and an outer major surface, and wherein the particle openings extend between the outer major surface and the inner major surface;
introducing a melt to at least a portion of the plurality of particle openings, the melt comprising at least 35 percent by weight Al 2 O 3 , based on the total weight of the melt, and a first metal oxide other than Al 2 O 3 , wherein the melt contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , based on the total weight of the melt;
and
at least partially cooling the melt in the particle openings to provide ceramic particles comprising glass, the glass comprising at least 35 percent by weight Al 2 O 3 , based on the total weight of the glass, and a first metal oxide other than Al 2 O 3 wherein the glass contains not more than 10 percent by weight collectively As 2 O 3 , B 2 O 3 , GeO 2 , P 2 O 5 , SiO 2 , TeO 2 , and V 2 O 5 , based on the total weight of the glass.
71. The method according to claim 70 , wherein the melt is introduced into the particle openings from the outer major surface of the roller such that the melt flows toward the inner major surface of the roller.
72. A method for making ceramic particles, the method comprising:
providing a roll comprising a plurality of particle openings, wherein the roller has an inner major surface and an outer major surface, and wherein the particle openings extend between the outer major surface to the inner major surface;
introducing a melt to at least a portion of the plurality of particle openings;
at least partially cooling the melt in the particle openings to provide ceramic particles comprising glass; and
heat-treating the ceramic particles to convert at least a portion of the glass to glass-ceramic particles, wherein the glass-ceramic has an average hardness of at least 13 GPa.
73. The method according to claim 72 , wherein the melt is introduced into the particles openings from the outer major surface of the roller such that the melt flows toward the inner major surface of the roller.