Highly resistant and ductile fiber concrete
A concrete in which metallic fibers are dispersed, obtained through mixing with water a composition including a cement; ultrafine elements with a pozzolanic reaction; granular elements distributed into two granular classes (C 1 )>1 mm and <5 mm and (C 2 ) ranges from 5 to 15 mm; cement additions; an amount of water E added in the mixture; a dispersant, and preferably a superplasticizer; metallic fibers, in an amount maximum equal to 120 kg per m 3 of concrete, the contents of the various components (a), (b), (C 1 ), (C 2 ), (d) and the amount of water E, expressed in volume, meeting the following relationships: ratio 1: 0.50≦(C 2 )/(C 1 )≦1.20; ratio 2: 0.25≦[(a)+(b)+(d)]/[(C 1 )+(C 2 )]≦0.60; ratio 3: 0.10≦(b)/(a)≦0.30; ratio 4: 0.05≦E/[(a)+(b)+(d)]≦0.75; ratio 5: (d)/(a)≦0.20. The invention applies to the manufacture of voussoirs without frameworks, of tiles and of elements of the plate, shell type or the like.
1. A concrete in which metallic fibres are dispersed, obtained through mixing with water a composition comprising:
(a) a cement with particles having a grain size D50 ranging from 10 to 20 μm;
(b) ultrafine elements with a pozzolanic reaction, element particles of said ultrafine elements having a grain size D50 of maximum 1 μm;
(c) granular elements distributed into two granular classes C 1 and C 2 defined as follows:
(C 1 ): particles with a size higher than 1 μm and lower than 5 mm,
(C 2 ): particles with a size ranging from 5 to 15 mm;
(d) cement additions with a grain size D50 lower than or equal to 100 μm;
(e) an amount of water E added;
(f) a dispersant or a superplasticizer, being present in a dry matter proportion ranging from 1.5 to 5% by volume based on the cement;
(g) metallic fibres, in an amount maximum equal to 120 kg per m 3 of concrete and having an individual length l such that the concrete has a l/φ ratio of at least 2, l being the fibre individual length and φ being the diameter of the biggest grain;
wherein contents of components (a), (b), (C 1 ), (C 2 ), (d) and the amount of water E, expressed in volume, meet the following relationships:
ratio 1: 0.50≦(C 2 )/(C 1 )≦1.20
ratio 2: 0.25≦[(a)+(b)+(d)]/[(C 1 )+(C 2 )]≦0.60
ratio 3: 0.10≦(b)/(a)≦0.30
ratio 4: 0.50≦E/[(a)+(b)+(d)]≦0.75
ratio 5: (d)/(a)≦0.20.
2. A concrete according to claim 1 , wherein:
a) the cement particles (a) have a grain size D50 of about 15 μm,
b) the ultrafine elements with a pozzolanic reaction (b) have a particle size D50 lower than 1 μm.
3. A concrete according to claim 1 or 2 , wherein the following relationship is obtained for ratio 2 of the contents of the components (a), (b), (C 1 ), (C 2 ), (d), expressed in volume:
ratio 2: 0.25≦[(a)+(b)+(d)]/[(C 1 )+(C 2 )]≦0.45
and wherein the concrete has a firm to fluid consistency.
4. A concrete according to claim 1 of 2 , wherein the following relationship is obtained for ratio 2 of the contents of the components (a), (b), (C 1 ), (C 2 ), (d), expressed in volume:
ratio 2: 0.45≦[(a)+(b)+(d)]/[(C 1 )+(C 2 )]≦0.60
and wherein the concrete has an autoconforming consistency.
5. A concrete according to claim 1 , wherein the following relationship are obtained for ratios 1, 3, 4, 5, of the contents of the components (a), (b), (C 1 ), (C 2 ), (d), and the amount of water E, expressed in volume:
ratio 1: 0.60≦(C 2 )/(C 1 )≦1.0
ratio 3: 0.15≦(b)/(a)≦0.25
ratio 4: 0.55≦E/[(a)+(b)+(d)]0.70
ratio 5: (d)/(a)≦0.15.
6. A concrete according to claim 1 , wherein the cement is a high silica content cement, said cement comprising at least 20% by weight of combined silica based on the cement weight.
7. A concrete according to claim 1 , wherein the amount of metallic fibres in the concrete ranges from 20 to 120 kg/m 3 of concrete.
8. A concrete according to claim 1 , wherein the metallic fibres are steel fibres.
9. A concrete according to claim 8 , wherein the steel fibres have a carbon content ranging from 0.7% to 0.8%.
10. A concrete according to claim 8 , wherein the steel fibres have a carbon content lower than or equal to 0.1%.
11. A concrete according to claim 1 , further comprising, fibres of polyvinyl alcohol, polyacrylonitrile, high density polyethylene, aramid polyamide or polypropylene.
12. A concrete according to claim 1 , further comprising a superplasticizer present in a dry matter proportion ranging from 1.5 to 5% by volume based on the cement.
13. A concrete according to claim 12 , wherein the superplasticizer is selected from the group consisting of polyoxyethylenated phosphonate, polyox polycarboxylates and mixtures thereof.
14. A concrete according to claim 1 , wherein it shows:
a flexure strength Rfl measured on prismatic samples, higher than or equal to 15 MPa,
a compression strength Rc measured on cylindrical samples, higher than or equal to 120 MPa,
said flexure strength and compression strength being evaluated at the end of a 28 day time.
15. A concrete according to claim 1 , wherein the ultrafine elements wit a pozzolanic reaction (b) comprise silica fumes.
16. A concrete according to claim 1 , wherein the granular elements (c) are sieved or ground granulates or mixtures of granulates.
17. A concrete according to claim 1 , wherein the cement additions (d) are fillers, quartz flour, hard chalk, fly ashes or slags.
18. Voussoirs, tiles, plate or shell elements, made from a concrete according to claim 1 .
19. A prefab element made from a concrete according to claim 1 .
20. A concrete according to claim 1 , wherein it is produced in a ready-to-use concrete plant.
21. A concrete according to claim 1 , wherein it is produced in a prefabrication plant.
22. A method for producing a concrete in which metallic fibres are dispersed, comprising mixing an amount of water E with a composition comprising:
(a) a cement with particles having a grain size D50 ranging from 10 to 20 μm;
(b) ultrafine elements with a pozzolanic reaction, element particles of said ultrafine elements having a grain size D50 of maximum 1 μm;
(c) granular elements distributed into two granular classes (C 1 ) and (C 2 ) defined as follows:
(C 1 ): particles with a size higher than 1 μm and lower than 5 mm,
(C 2 ): particles with a size ranging from 5 to 15 mm;
(d) cement additions with a grain size D50 lower than or equal to 100 μm;
(e) a dispersant or a superplasticizer, present in a dry matter proportion ranging from 1.5 to 5% by volume based on the cement;
(f) metallic fibres in an amount maximum equal to 120 kg per m 3 of concrete and having an individual length l such that the concrete has a l/φ ratio of at least 2, l being the individual length of the fibres and φ being the diameter of the biggest grain;
wherein contents of components (a), (b), (C 1 ), (C 2 ), (d) and the amount of water E, expressed in volume, meet the following relationships:
ratio 1: 0.50≦(C 2 )/(C 1 )≦1.20
ratio 2: 0.25≦[(a)+(b)+(d)]/[(C 1 )+(C 2 )]≦0.60
ratio 3: 0.10≦(b)/(a)≦0.30
ratio 4: 0.50≦E/[(a)+(b)+(d)]≦0.75
ratio 5: (d)/(a)≦0.20.
23. A method according to claim 22 , wherein:
a) the cement particles (a) have a grain size D50 of about 15 μm , and
b) the ultrafine elements with a pozzolanic reaction (b) have a particle size D50 lower than 1 μm.
24. A method according to claim 22 or 23 , wherein the following relationship is obtained for ratio 2 of components (a), (b), (C 1 ), (C 2 ), (d), expressed in volume
ratio 2: 0.25≦[(a)+(b)+(d)]/[(C 1 )+(C 2 )]≦0.45
and wherein the concrete has a firm to fluid consistency.
25. A method according to claim 22 or 23 , wherein the following relationship is obtained for ratio 2 of the contents of the components (a), (b), (C 1 ), (C 2 ), (d), expressed in volume:
ratio 2: 0.45≦[(a)+(b)+(d)]/[(C 1 )+(C 2 )]≦0.60
and wherein the concrete is an autoconforming concrete.
26. A method according to claim 22 , wherein the following relationships a obtained for ratios 1, 3, 4, 5, of the contents of the components (a), (b), (C 1 ), (C 2 ), (d), and the amount of water E, expressed in volume:
ratio 1: 0.60≦(C 2 )/(C 1 )≦1.0
ratio 3: 0.15≦(b)/(a)≦0.25
ratio 4: 0.55≦E/[(a)+(b)+(d)]≦0.70
ratio 5: (d)/(a)≦0.15.
27. A method according to claim 22 , wherein the cement is a high silica content cement, said cement comprising at least 20% by weight of combined silica based on the cement weight.
28. A method according to claim 22 , wherein the amount of metallic fibres in the concrete ranges from 20 to 120 kg/m 3 of concrete.
29. A method according to claim 22 , wherein the metallic fibres are steel fibres.
30. A method according to claim 22 , wherein the steel fibres have a carbon content ranging from 0.7% to 0.8%.
31. A method according to claim 29 , wherein the steel fibres have a carbon content, lower than or equal to 0.1%.
32. A method according to claim 22 , further comprising mixing into the composition fibres of polyvinyl alcohol, polyacrylonitrile, high density polyethylene, aramid polyamide or polypropylene.
33. A method according to claim 22 , utilizing a superplasticizer, present in a dry matter proportion ranging from 1.5 to 5% by volume based on the cement.
34. A method according to claim 22 , wherein the superplasticizer is selected from the group consisting of polyoxyethylenated phosphonate, polyox polycarboxylates and mixtures thereof.
35. A method according to claim 22 , wherein the concrete shows:
a flexure strength Rfl measured on prismatic samples, higher than or equal to 15 MPa, and
a compression strength Rc measured on cylindrical samples, higher than or equal to 120 MPa,
said flexure strength and compression strength being evaluated at the end of a 28 day time.
36. A method according to claim 22 , wherein the ultrafine elements with a pozzolanic reaction (b) comprise silica fumes.
37. A method according to claim 22 , wherein the granular elements (c) are sieved or ground granulates or mixtures of granulates.
38. A method according to claim 22 , wherein the cement additions (d) are fillers, quartz flours, hard chalk, fly ashes or slags.