Use of tin derivatives as catalysts
The invention concerns the use as catalyst for transforming carbamates of compounds corresponding to the general formula (I): —Sn (X) (X′) wherein: X′ is selected among chloride, bromide, iodide, thiocyanate radicals, sulphonate radicals, advantageously perfluorinated on the carbon bearing the sulphonate function; X is selected among the values of X′ and among radicals of formula Y-Z; Y is selected among the chalcogen groups, advantageously light (that is oxygen and sulphur); Z is selected in the group consisting of trisubstituted tin, monosubstituted zinc, and the oxygenated acid radicals after ignoring the OH function. The invention is applicable to the coating industry.
1. A transcarbamation process, comprising the step of reacting a carbamate vith an alcohol in the presence of an efficient catalytic amount, as transcarbamation catalyst, of compounds of general formula (I):
wherein:
X′ is chloride, bromide, iodide, thiocyanate radicals or sulfonate radicals;
X is X′ or radicals of formula Y-Z;
Y is a chalcogen; and
Z is trisubstituted tin, monosubstituted zinc or groups of oxygen-comprising acids, without the OH functional group.
2. The transcarbamation process according to claim 1 , wherein:
the X′ sulfonate radicals are perfluorinated on the carbon carrying the sulfonate functional group; and
Y is oxygen or sulfur.
3. The transcarbamation process according to claim 1 , wherein the catalyst is used in an amount of at least equal to 0.5% and at most equal to 5% as carbamate functional group equivalent.
4. The transcarbamation process according to claim 3 , wherein the amount is between 1% and 2%.
5. The transcarbamation process according to claim 1 , wherein X is X′.
6. The transearbamation process according to claim 1 , wherein one or more of the X or X′ groups are halides or thiocyanates.
7. The transcarbamation process according to claim 1 , wherein Z has the formula:
wherein X′ is as above defined.
8. The process according to claim 1 , wherein the transcarbamation reaction is carried out at a temperature of between 100 and 200° C.
9. The process according to claim 8 , wherein the temperature is between 120 and 180° C.
10. The process according to claim 1 , wherein X′ is a sulfonate radical perfluorinated on the carbon carrying the sulfonate functional group, and Y oxygen or sulfur.
11. A composition, comprising at least one carbamate capable of being obtained by reaction of a hydroxylated compound with an isocyanate and at least one compound of following general formula (I):
wherein:
X′ are sulfonate radicals:
X is X′ or radicals of formula Y-Z; and
Z is trisubstituted tin, monosubstituted zinc or groups of oxygen-comprising acids, without the OH functional group, wherein the isocyanate is aliphatic, the X′ sulfonate radicals are perfluorinated on the carbon carrying the sulfonate functional group; and
Y is oxygen or sulfur.
12. The composition according to claim 11 , further comprising an alcohol or polyalcohol.
13. The composition according to claim 12 , wherein the alcohol or polyalcohol is primary.
14. The composition according to claim 12 , wherein the hydroxylated compound is an alcohol volatile at a temperature at least equal to 150° C. or a hydroxylated masking agent.
15. The composition according to claim 14 , wherein the masking agent is a phenol or an oxime.
16. The composition according to claim 12 , wherein the hydroxylated compound is methanol.
17. The composition according to claim 11 , wherein wherein X′ is a sulfonate radical perfluorinated on the carbon carrying the sulfonate functional group, and Y oxygen or sulfur.