Lead-free solder powder material, lead-free solder paste and a method for preparing same

1. A method for preparing lead-free solder powder material comprising the steps of:

positioning a quantity of solder metal powder material comprised of two or more metals capable of forming an intermetallic compound and a plurality of metal balls in a sealed container; and

moving said metal balls in said sealed container to finely grind said solder metal powder material of said two or more metals to provide a lead-free solder metal powder material including an unreacted phase and an amorphous phase.

2. The method for preparing a lead-free solder powder material according to claim 1 , wherein both of said two or more metals capable of forming an intermetallic compound are simple substances of metals selected from the group consisting of tin (Sn), silver (Ag), copper (Cu), bismuth (Bi), zinc (Zn), indium (In), gold (Au), nickel (Ni), antimony (Sb), palladium (Pd), platinum (Pt), and germanium (Ge).

3. The method for preparing a lead-free solder powder material according to claim 1 , wherein said two or more metals capable of forming an intermetallic compound are a combination of an alloy including at least one selected from the group consisting of tin (Sn), silver (Ag), copper (Cu), bismuth (Bi), zinc (Zn), indium (In), gold (Au), nickel (Ni), antimony (Sb), palladium (Pd), platinum (Pt), and germanium (Ge) and a metal which is capable of forming an intermetallic compound with said alloy.

4. The method for preparing a lead-free solder powder material according to claim 1 wherein said two or more metals capable of forming an intermetallic compound comprises a combination selected from the group consisting of Cu—Sn, Ag—Sn, Au—Sn, Au—Cu, Au—Bi, Au—Zn, Au—In, Au—Sb, Au—Pt, Ni—Sn, Cu—In, Ni—In, Ag—In, Ag—Sb, Ag—Pt, Ag—Zn, Bi—In, Ni—Bi, Cu—Zn, Cu—Sb, Cu—Ge, Cu—Pd, Cu—Pt, Ge—Ni, In—Pd, In—Sb, Ni—Zn, Ni—Sb, Ni—Pt, Pd—Sn, Pt—Sn, Pt—Sb, and Sb—Zn.

5. The method for preparing lead-free solder powder material according to claim 1 wherein the particle diameter of said solder metal powder material is in a range from about 10 nanometers to 100 micrometers.

6. A method of preparing a lead-free solder powder material, comprising the steps of:

positioning a powder including two or more metals capable of forming an intermetallic compound in a high energy mill; and

high energy milling said powder to form a finely ground mixture including an unreacted phase and a reacted phase; and

wherein said reacted phase includes a crystal phase and an amorphous phase.

7. The method of claim 6 , wherein said high energy milling comprises milling said two or more metals in a vibrating ball mill at 13.1 Hz for five hours.

8. The method of claim 7 , wherein after said milling said material has a lower melting point that a finely ground mixture of said two or more metals that does not include said unreacted and said amorphous phases.