Protective layer against wear based on artificial resin, method for the production thereof and use of the same
The invention relates to a protective layer against wear based on artificial resin. Hard particles ( 1 ) having a hardness of at least 6 on the Mohs scale are embedded in said layer, as are compact, round, solid particle ( 2 ), which are essentially free of sharp edges and have a hardness of at least 5 on the Mohs scale. The grain size distribution of the round solid particles ( 2 ) begins at least with the smallest grain diameter of the hard particles ( 1 ) and reaches a maximum of five times the value of the largest hard particle diameter, the average grain diameter of the solid particles ( 2 ) being larger than the average grain diameter of the hard particles ( 1 ). The hard particles and round solid particles are admixed for producing a protective layer against wear and for providing wear-resistant surfaces.
1. A coating comprising embedded hard solid particles with a Mohs hardness of at least 6, and solid spherical particles substantially without cutting edges and with a Mohs hardness of at least 5, wherein the particle size distribution of the solid spherical particles extends from the smallest particle diameter of the hard particles to less than five times the largest particle diameter of the hard particles, and the average particle diameter of the solid spherical particles is greater than the average particle diameter of the hard particles.
2. The coating according to claim 1 wherein the particle size distribution of the solid spherical particles starts within the range between lowest and largest particle diameter of the hard particles and ends about 1.5 times of the largest particle diameter of the hard particles.
3. The coating according to claim 1 wherein the solid spherical particles are monodisperse, having a median diameter about 1.2 times the largest particle diameter of the hard particles.
4. The coating according to claim 1 , wherein the solid spherical particles comprise transparent glass spheres, beads or a mixture thereof.
5. Method for the production of a coating according to claim 1 comprising applying a homogenous coating composition comprising the hard particles and the solid spherical particles in a synthetic resin to a substrate.
6. The method according to claim 5 wherein the substrate is an overlay paper that is soaked with the coating composition and subsequently pressed onto a surface.
7. The coating according to claim 1 wherein the volume share of the solid spherical particles is from 5 to 40 volume percent relative to the total volume percent of hard particles and solid spherical particles.
8. The coating according to claim 7 wherein the amount of the solid spherical particles is from 10 to 30 volume percent relative to the total volume percent of hard particles and solid spherical particles.
9. Method of protecting surfaces, floors, slabs, transform plates by forming the coating according to claim 1 .
10. A protected article comprising the coating of claim 1 and further comprising a reflective surface as a safety marker.
11. The coating according to claim 1 wherein the solid particles are radiant glass beads and the solid particles comprise from 40 to 70 volume percent relative to the total volume percent of particles in the coating.
12. A coating composition comprising:
hard particles with a Mohs hardness of at least 6;
solid particles with a Mohs hardness of at least 5, wherein the median particle size of the solid particles is greater than the median particle size of the hard particles; and
a polymeric resin.
13. The composition according to claim 12 wherein the solid particles are spherical particles with essentially no cutting edges.
14. The composition according to claim 12 wherein the solid particles are glass spheres or glass beads.
15. The composition according to claim 12 comprising from 5 to 40 volume percent of the solid particles relative to the total volume percent of particles in the polymeric resin.
16. The composition according to claim 12 wherein the solid particles have a median diameter from about 1.2 to 1.36 times the largest particle diameter of the hard particles.
17. The composition according to claim 12 wherein the solid particles have a median diameter of about 1.2 times the largest particle diameter of the hard particles.
18. The composition according to claim 12 wherein the solid particles are radiant glass beads and the solid particles comprise from 40 to 70 volume percent relative to the total volume percent of particles.
19. An article comprising a cured coating composition of claim 18 wherein the coating provides a reflective surface on the article, and the article functions as a safety marker.