Modified polyolefin films
Disclosed are techniques and related material blends for improving adhesion between a polyolefin film and a pressure sensitive adhesive, and also significantly decreasing the coefficient of thermal expansion of a polyolefin film by modifying the chemical properties of the film. Specifically, particular amounts of a modifying polymer and/or copolymer such as ethylene vinyl acetate are incorporated into the polyolefin film. The polyolefin film may for instance be either a polyethylene or polypropylene film.
1. A method for improving adhesive strength of a polyolefin film and a pressure sensitive adhesive, said method comprising:
providing a polyolefin for subsequent use in forming a film, said polyolefin being selected from the group consisting of polyethylene, polypropylene, and copolymers thereof;
providing an effective amount of ethylene vinyl acetate;
blending said ethylene vinyl acetate and said polyolefin to form a modified blend;
forming a film from said modified blend, wherein said film exhibits improved bonding characteristics with adhesives applied to said film.
2. The method of claim 1 wherein said effective amount of said ethylene vinyl acetate in said polyolefin is from about 1% to about 50%.
3. The method of claim 2 wherein said effective amount is from about 7.5% to about 30%.
4. The method of claim 3 wherein said effective amount is about 30%.
5. The method of claim 1 wherein said polyolefin is polyethylene and said polyethylene is selected from the group consisting of low density polyethylene, linear low density polyethylene, high density polyethylene, ultra-low density polyethylene, ethylene plastomers, ultra-high molecular weight polyethylene, and combinations thereof.
6. The method of claim 1 further comprising:
providing a grafted polyolefin selected from the group consisting of (i) polyethylene with silicone, (ii) ethylene n-butyl acrylate, (iii) ethylene methyl acrylate, and combinations thereof; and
incorporating said grafted polyolefin with said modified blend.
7. A method for decreasing the thermal expansion characteristics of a polyolefin material, said method comprising:
providing a polyolefin material, wherein said polyolefin is selected from the group consisting of polyethylene, polypropylene, and copolymers thereof;
blending from about 1% to about 50% of ethylene vinyl acetate in said polyolefin material to thereby decrease the thermal expansion characteristics of said polyolefin material.
8. The method of claim 7 wherein said effective amount is from about 7.5% to about 30% of said ethylene vinyl acetate is incorporated in said polyolefin material.
9. The method of claim 7 wherein about 30% of said ethylene vinyl acetate is incorporated in said polyolefin material.
10. The method of claim 7 wherein said polyolefin is polyethylene and said polyethylene is selected from the group consisting of low density polyethylene, linear low density polyethylene, high density polyethylene, ultra-low density polyethylene, ethylene plastomers, ultra-high molecular weight polyethylene and combinations thereof.
11. The method of claim 7 further comprising:
providing a grafted polyolefin selected from the group consisting of (i) polyethylene with silicone, (ii) ethylene n-butyl acrylate, (iii) ethylene methyl acrylate, and combinations thereof; and
incorporating said grafted polyolefin with said modified blend.
12. A polyolefin blend consisting essentially of (i) a polyolefin selected from the group consisting of polyethylene, polypropylene, and copolymers thereof, and (ii) from about 1% to about 50% based on the weight of said polyolefin of ethylene vinyl acetate, wherein said resulting polyolefin blend exhibits improved bonding characteristics and reduced thermal expansion characteristics.
13. The blend of claim 12 wherein the amount of ethylene vinyl acetate is from about 7.5% to about 30%.
14. The blend of claim 12 wherein the amount of ethylene vinyl acetate is about 30%.
15. The blend of claim 12 wherein the polyolefin is polyethylene.
16. The blend of claim 15 wherein the polyethylene is selected from the group consisting of low density polyethylene, linear low density polyethylene, high density polyethylene, ultra-low density polyethylene, ethylene plastomers, ultra-high molecular weight polyethylene and combinations thereof.
17. The blend of claim 12 wherein said polyolefin is linear low density polyethylene and the amount of said ethylene vinyl acetate is 30%.
18. The blend of claim 12 wherein said polyolefin is polyethylene and the softening point of said polyethylene is more than 40° C. higher than the softening point of said ethylene vinyl acetate.