Process for the preparation of aqueous suspensions of anionic colloidal silica having a neutral pH and applications thereof
View Patent ↗The instant invention relates to a process for the preparation of an aqueous suspension of anionic colloidal silica having a neutral pH which is stable over time and comprises individualized particles of colloidal silica which are not bound to one another by siloxane bonds. The instant suspensions show high storage stability and are particularly useful for the clarification of beer, for the preparation of cosmetic formulations, for the production of ink for printers, for paints and for anticorrosive treatments.
1. A process for the preparation of an aqueous suspension of anionic colloidal silica having a neutral pH ranging from 6-8, which is stable for greater than six months and comprising individualized particles of colloidal silica which are not bound to one another by siloxane bonds, wherein an aqueous suspension of anionic colloidal silica comprising individualized particles of colloidal silica which are not bound to one another by siloxane bonds and having a pH in the range from 8.5 to 11, a specific surface in the range from 20 m 2 /g to 700 m 2 /g, a particle diameter in the range from 4 nm to 150 nm and having a percentage of silica of ≧5 parts by weight, is reacted with an aqueous suspension of anionic colloidal silica comprising individualized particles of colloidal silica which are not bound to one another by siloxane bonds having a pH in the range from 2 to 3.5, a specific surface in the range from 20 m 2 /g to 700 m 2 /g, a particle diameter in the range from 4 nm to 150 nm and having a percentage of silica of ≧5 parts by weight, further where the diameter of the particle is unchanged by the process.
2. A process according to claim 1 , where said aqueous suspension of anionic colloidal silica having a pH in the range from 8.5 to 11 and containing 5 to 200 parts of silica expressed as dry matter is reacted with an aqueous suspension of anionic colloidal silica having a pH in the range from 2 to 3.5 and containing 100 parts of silica expressed as dry matter.
3. The process of claim 1 wherein the aqueous suspension of anionic colloidal silica having a neutral pH has a silica content of at least 5% by weight.
4. The process of claim 1 wherein the aqueous suspension of anionic colloidal silica having a neutral pH has a silica content of about 25 to 30% by weight.
5. The process of claim 1 wherein the individualized particles of anionic colloidal silica having a neutral pH range from 4 nm to 100 nm.
6. The process of claim 1 wherein the individualized particles of anionic colloidal silica having a neutral pH range from 4 nm to 50 nm.
7. The process of claim 1 wherein the individualized particles of anionic colloidal silica having a neutral pH range from 5 nm to 50 nm.
8. The process of claim 1 wherein the individualized particles of anionic colloidal silica having a neutral pH range from 9 nm to 50 nm.