Filler composition for high yield strength base metals
A weld wire of the present invention comprises a steel sheath encapsulating a fluxed core having a combination of fluxing compounds and alloying elements. The fluxing compounds comprise up to 2% Wt of fluoride compounds and up to 49% Wt of oxide compounds. The alloying elements comprise Mn, Ni, Co, Ti and up to about 0.98% Wt of C. The amount of Co is sufficient to produce a ferrite-bainite weld metal morphology of a resulting weld. A yield strength of the resulting weld was measured from about 95 ksi to about 111 ksi.
1. A weld wire for use in a flux-cored arc welding (FCAW) process of welding high strength steel, comprising:
a fluxed core including, by weight:
alloying elements comprising (i) about: 11-13% of Ni and 11-16% of Fe, and (ii) up to about: 1% of C, 4.98% of Co, 0.1% of B, and 0.25% of Zr; and
fluxing compounds comprising: (i) about 0.5-2% of metal fluorides and (ii) about 20-49% of oxides; and
a steel sheath encapsulating the fluxed core, wherein an amount of Co in the fluxed core of the weld wire is used in the FCAW process of welding the high strength steel for controlling a fine-grained morphology of acicular ferrite-bainite in a produced weld metal.
2. The weld wire of claim 1 , wherein the alloying elements further comprise about 12-20% of Mn and up to about: 1% of Ti, 2% of Mg, and 3.0% of Si.
3. The weld wire of claim 1 , wherein the steel sheath comprises, by weight, up to about: 0.02% of C and 0.5% of Mo.
4. The weld wire of claim 1 , wherein the alloying elements comprise 11.18% of Ni.
5. The weld wire of claim 1 , wherein the alloying elements comprise 11.1-11.9% of Fe.
6. The weld wire of claim 1 , wherein the alloying elements comprise 0.98% of C.
7. The weld wire of claim 1 , wherein the alloying elements comprise 4.98% of Co.
8. The weld wire of claim 1 , wherein the alloying elements comprise 0.06% of B.
9. The weld wire of claim 1 , wherein the alloying elements comprise 0.00% of B.
10. The weld wire of claim 1 , wherein the alloying elements comprise 0.23% of Zr.
11. The weld wire of claim 1 , wherein the fluxing compounds comprise about 1.9-2.0% of metal fluorides.
12. The weld wire of claim 11 , wherein the fluxing compounds comprise 1.96-1.98% of metal fluorides.
13. The weld wire of claim 1 , wherein the fluxing compounds comprise about 45-49% of oxides.
14. The weld wire of claim 13 , wherein the fluxing compounds comprise 47.4-47.9% of oxides.