Process for preparing alkyl hydroxyalkyl cellulose ethers
The process for preparing an alkyl hydroxyalkyl cellulose ether comprises the steps of: a) alkalizing cellulose to obtain alkali cellulose, b) reacting alkali cellulose with an alkyl halogenide until an alkyl cellulose ether with a D.S.(alkyl) value of from 0.7 to 2.5. is attained, c) removing excess alkyl halogenide from the reaction mixture, and d) reacting the alkyl cellulose ether with an alkylene oxide in a liquid suspending agent to produce an alkyl hydroxyalkyl cellulose ether. An alkyl hydroxyalkyl cellulose ether is produced which has an D.S.(alkyl) of from 0.7 to 2.5 and an MS (hydroxyalkyl) from 0.03 to 2.0, wherein not more that 15 percent of the hydroxyalkyl groups are capped with an alkyl group.
1. A process for preparing an alkyl hydroxyalkyl cellulose ether comprising the steps of:
a) alkalizing cellulose to obtain alkali cellulose,
b) reacting alkali cellulose with an alkyl halogenide until an alkyl cellulose ether with a D.S.(alkyl) value of from 0.7 to 2.5 is attained,
c) removing excess alkyl halogenide from the reaction mixture, and
d) reacting the alkyl cellulose ether with an alkylene oxide in a liquid suspending agent to produce an alkyl hydroxyalkyl cellulose ether, wherein the weight ratio between the alkylene oxide and the liquid suspending agent is from 0.001:1 to 1:1 and the liquid suspending agent is a blend comprising from 10 to 90 weight percent of an alcohol and from 90 to 10 weight percent of an aromatic or aliphatic hydrocarbon.
2. The process of claim 1 wherein in step b) alkali cellulose is reacted with an alkyl halogenide until an alkyl cellulose ether with a D.S.(alkyl) value of from 0.8 to 2.2 is attained.
3. The process of claim 1 wherein excess alkali metal hydroxide is removed in step c).
4. The process of claim 1 wherein in step d) the alkyl cellulose ether is reacted with the alkylene oxide until an alkyl hydroxyalkyl cellulose ether with an M.S.(hydroxyalkyl) value of from 0.03 to 2.0 is attained.
5. The process of claim 1 wherein step d) is carried out in a blend of isopropanol and n-hexane as a suspending agent.
6. The process of claim 1 wherein the alkyl halogenide in step b) is methyl chloride and the alkylene oxide in step d) is propylene oxide.
7. The process of claim 1 wherein the alkyl halogenide in step b) is methyl chloride and the alkylene oxide in step d) is ethylene oxide.
8. The process of claim 1 wherein steps b) and d) are carried out in separate reactors.
9. A process for preparing an alkyl hydroxyalkyl cellulose ether comprising the steps of:
a) alkalizing cellulose to obtain alkali cellulose,
b) reacting alkali cellulose with an alkyl halogenide until an alkyl cellulose ether with a D.S.(alkyl) value of from 0.7 to 2.5 is attained,
c) removing excess alkyl halogenide and excess alkali metal hydroxide from the reaction mixture, and
d) reacting the alkyl cellulose ether with an alkylene oxide in a liquid suspending agent to produce an alkyl hydroxyalkyl cellulose ether, wherein the liquid suspending agent is a blend comprising from 10 to 90 weight percent of an alcohol and from 90 to 10 weight percent of an aromatic or aliphatic hydrocarbon.
10. The process of claim 9 wherein the suspending agent in step d) is a blend of isonropanol and n-hexane.