Method for the production of polybutylene terephthalate
In a process of producing PBT, a mixture of BDO and TPA is esterified in the presence of a catalyst solution, and the esterification product is polycondensated. To avoid the formation of deposits in the PBT, the catalyst solution contains 0.05 to 10 wt-% alkyl titanate, 85 to 99 wt-% BDO, 50 to 50,000 ppm bifunctional carboxylic acid equivalents and/or monofunctional hydroxycarboxylic acid equivalents and not more than 0.5 wt-% water.
1. A process of producing polybutylene terephthalate (PBT) from butanediol (BDO) and terephthalic acid (TPA), in which a mixture of BDO and TPA is subjected to an esterification in the presence of a catalyst solution containing alkyl titanate at temperatures in the range from 130 to 260° C. and the product of the esterification is subjected to a polycondensation, wherein the catalyst solution contains 0.05 to 10 wt-% alkyl titanate, 85 to 99 wt-% BDO, 50 to 50,000 ppm dicarboxylic acid and/or hydroxycarboxylic acid and/or monohydroxyalkyl dicarboxylic acid and not more than 0.5 wt-% water.
2. A process of producing polybutylene terephthalate (PBT) from butanediol (BDO) and dimethyl terephthalate (DMT), in which a mixture of BDO and DMT is subjected to a transesterification in the presence of a catalyst solution containing alkyl titanate and the product of the transesterification is subjected to a polycondensation, wherein the catalyst solution contains 0.05 to 10 wt-% alkyl titanate, 85 to 99 wt-% BDO, 50 to 50,000 ppm dicarboxylic acid and/or hydroxycarboxylic acid and/or monohydroxyalkyl dicarboxylic acid and not more than 0.5 wt-% water.
3. The process as claimed in claim 1 or 2 , wherein the content of dicarboxylic acid and/or hydroxycarboxylic acid and/or monohydroxyalkyl dicarboxylic acid is 50 to 30,000 ppm.
4. The process as claimed in claim 1 or 2 , wherein that BDO is mixed with alkyl titanate at temperatures of 50 to 230° C. and dicarboxylic acid and/or hydroxycarboxylic acid and/or monohydroxyalkyl dicarboxylic acid is added to this mixture to form said catalyst solution.
5. The process as claimed in claim 1 or 2 , wherein BDO is mixed with dicarboxylic acid and/or hydroxycarboxylic acid and/or monohydroxyalkyl dicarboxylic acid at temperatures of 50 to 230° C. and alkyl titanate is added to this mixture to form said catalyst solution.
6. The process as claimed in claim 1 , wherein a vapor mixture containing BDO, water and dicarboxylic acid is withdrawn from the esterification stage, water optionally together with low-boiling components is separated by distillation, and alkyl titanate is admixed to the higher-boiling condensate at a temperature of 50 to 230° C.
7. The process as claimed in claim 1 or 2 , wherein said dicarboxylic acid is selected from the group consisting of terephthalic acid, isophtalic acid, oxalic acid, malonic acid, succinic acid, and mixtures thereof.
8. The process as claimed in claim 1 or 2 , wherein said hydroxycarboxylic acid is selected from the group consisting of 3-hydroxybenzoic acid, 4-hydroxybenzoic acid, 3-hydroxybutyric acid, hydroxypropanoic acid, glycolic acid and mixtures thereof.
9. The process as claimed in claim 1 or 2 , wherein said monohydroxyalkyl dicarbonic acid is monohydroxybutyl terephthalic acid.
10. The process as claimed in claim 1 or 2 , wherein said alkyl-titanate is tetrabutyl orthotitanate.
11. The process as claimed in claim 1 or 2 , wherein said catalyst solution is additionally introduced in at least one polycondensation stage subsequent to the esterification stage.