Coating composition and article coated with the composition

1. A coating composition comprising:

(1) an anionic surfactant comprising a sulfonic acid salt;

(2) inorganic oxide microparticles;

(3) a silicon compound, having one acryl group or methacryl group and a hydrolyzable group, or a hydrolysate of the compound;

(4) a compound having at least two photopolymerizable unsaturated groups; and

(5) a photopolymerization initiator.

2. The coating composition as set forth in claim 1 wherein, as non-volatile matter,

the content of said component of (1) is 3 to 10% by weight,

the content of said component of (2) is 30 to 70% by weight,

the content of said component of (3) is 2 to 20% by weight,

the content of said component of (4) is 8 to 64% by weight,

and the content of said component of (5) with respect to 100 weight parts of the total of said components of (1) to (4) is 1 to 100 weight parts.

3. The coating composition as set forth in claim 1 , wherein the anionic surfactant comprising a sulfonic acid salt is at least one surfactant selected from the group consisting of: dialkyl sulfosuccinic acid ester salts, alkyl sulfosuccinic acid dibasic salts, polyoxyethylene alkyl sulfosuccinic acid dibasic salts, sulfosuccinic acid half-ester salts, alkyl sulfoacetic acid salts, alkene (C 8 to C 30 ) monosulfonic acid salts, hydroxyalkane (C 8 to C 24 ) monosulfonic acid salts, N-acylmethyltaurine salts, secondary higher alcohol ethoxysulfates, sulfuric acid ester salts of aliphatic acid alkylolamides, higher alcohol sulfuric acid ester salts, secondary higher alcohol sulfuric acid ester salts, polyoxyethylene alkyl ether sulfuric acid salts, and monoglyceride sulfates.

4. The coating composition as set forth in claim 1 , wherein the inorganic oxide microparticles are microparticles of an oxide of at least one element selected from the group consisting of silicon (Si), aluminum (Al), tin (Sn), antimony (Sb), tantalum (Ta), cerium (Ce), lanthanum (La), iron (Fe), zinc (Zn), tungsten (W), zirconium (Zr), indium (In), and titanium (Ti).

5. The coating composition as set forth in claim 1 , wherein a particle size of the inorganic oxide microparticles is in the range of 1 to 100 nm.

6. The coating composition as set forth in claim 1 , wherein the inorganic oxide microparticles are surface modified by an organosilicon compound or organic compound.

7. The coating composition as set forth in claim 1 , wherein the silicon compound having one acryl group or methacryl group and a hydrolyzable group, or a hydrolysate of the compound is a silicon compound or hydrolysate thereof that is expressed by the general formula:

R 1 R 2 a Si(OR 3 ) 3-a

(where R 1 is a group containing one acryl or methacryl group with 2 to 12 carbon atoms, R 2 is an alkyl group, aryl group, alkenyl group, halogenated alkyl group, or halogenated aryl group with 1 to 6 carbon atoms, the R 3 of the hydrolyzable group OR 3 is hydrogen atoms, or an alkyl group, acyl group, or alkylacyl group with 1 to 4 carbon atoms, and a=0, 1, or 2).

8. The coating composition as set forth in claim 1 , wherein the compound having at least two photopolymerizable unsaturated groups is a compound having at least two functional groups selected from the group consisting of the acryl and methacryl groups, vinyl group, aryl group, epoxy group, thiol group, an episulfide group.

9. An article obtained by coating the coating composition as set forth in claim 1 onto a base and performing photo-curing.