Method for producing electroconductive particles
The purpose of the invention is to provide a method for producing conductive fine particles having a plating layer of extremely uniform thickness and free from scratches without being accompanied with agglomeration of fine particles to be plated during the plating process and a method for producing conductive fine particles comprising resin fine particles and a tin/silver alloy plating layer formed thereon. The invention is a method for producing a conductive fine particle, which comprises forming a plating layer on the surface of a fine particle to be plated using a barrel plating apparatus having a rotatable barrel in a plating bath, said method comprising putting the fine particle to be plated and a dummy particle with a lager particle diameter than that of the fine particle to be plated in the barrel and forming a plating layer while vibrating the barrel at an amplitude of 0.05 to 3.0 mm and a frequency of 20 to 120 Hz.
1. A method for producing a conductive fine particle,
which comprises forming a plating layer on the surface of an organic resin fine particle having a conductive base layer on the surface using a barrel plating apparatus having a rotatable barrel in a plating bath,
said method comprising putting the organic resin fine particle and a dummy particle in the barrel and forming a plating layer while vibrating the barrel at an amplitude of 0.05 to 3.0 mm and a frequency of 20 to 120 Hz,
wherein the organic resin fine particle is made of at least one resin selected from the group consisting of network structure polymer, thermosetting resin and elastic body,
wherein the dummy particle has a particle diameter of 2 to 50 times as large as that of the organic resin fine particle and a specific gravity of 1.0 to 12.0 times as heavy as that of the organic resin fine particle,
wherein a feed amount of the fine particle to be plated into the barrel is 10 to 60% by volume of the capacity of the barrel,
a feed amount of the dummy particle into the barrel is 10 to 70% by volume relative to the total of the feed amount of the fine particle to be plated and the feed amount of the dummy particle, and
a volume of the mixture of the fine particle to be plated and the dummy particle fed into the barrel is 10 to 60% by volume of the capacity of the barrel.