Nitrogen containing metal powder, production process therefor, and porous sintered body and solid electrolytic capacitor using same
A nitrogen containing metal powder wicth a large specific surface area, and containing a suitable quantity of nitrogen dispersed uniformly within the metal is produced with good productivity, and provides a solid electrolytic capacitor with a high capacitance, minimal leakage current, and excellent long term reliability. This nitrogen containing metal powder has a ratio W/S between the nitrogen content W [ppm] of the powder, and the specific surface area S [m 2 /g], as measured by a BET method, that falls within a range from 500 to 3000. This type of powder can be produced by a process in which a metal salt containing the metal is reacted with a reducing agent and undergoes reduction within a diluent salt, thereby generating the metal, wherein a nitrogen containing gas is introduced into the space contacting the reaction melt comprising the metal salt, the reducing agent and the diluent salt, thereby generating the metal and incorporating the nitrogen within the metal.
1. A nitrogen containing metal powder comprising a metal powder that contains nitrogen, wherein a ratio W/S between a nitrogen content W [ppm], and a specific surface area S [m 2/ g], as measured by a BET method, is within a range from 500 to 3000.
2. A nitrogen containing metal powder according to claim 1 , wherein said nitrogen exists as a solid solution within said metal.
3. A nitrogen containing metal powder according to claim 1 , wherein said metal is at least one metal selected from a group consisting of niobium, tantalum, and niobium-tantalum alloy.
4. A production process for a nitrogen containing metal powder according to claim 1 , in which a metal salt containing said metal is reacted with a reducing agent and undergoes reduction within a molten diluent salt, thereby generating said metal, wherein
a nitrogen containing gas is introduced into a space contacting a reaction melt comprising said metal salt, said reducing agent and said diluent salt,
thereby generating said metal and incorporating said nitrogen within said metal.
5. A production process for a nitrogen containing metal powder according to claim 3 , in which a metal salt containing said metal is reacted with a reducing agent and undergoes reduction within a molten diluent salt, thereby generating said metal, wherein
a nitrogen containing gas is introduced into a space contacting a reaction melt comprising said metal salt, said reducing agent and said diluent salt,
thereby generating said metal and incorporating said nitrogen within said metal.
6. A production process for a nitrogen containing metal powder according to claim 4 , wherein said metal salt is a potassium fluoride salt of at least one of niobium and tantalum, and said reducing agent is sodium.
7. A production process for a nitrogen containing metal powder according to claim 5 , wherein said metal salt is a potassium fluoride salt of at least one of niobium and tantalum, and said reducing agent is sodium.
8. A production process for a nitrogen containing metal powder according to claim 4 , wherein said reducing agent and said metal salt are each added either continuously or in portions to said diluent salt.
9. A production process for a nitrogen containing metal powder according to claim 5 , wherein said reducing agent and said metal salt are each added either continuously or in portions to said diluent salt.
10. A production process for a nitrogen containing metal powder according to claim 6 , wherein said reducing agent and said metal salt are each added either continuously or in portions to said diluent salt.
11. A production process for a nitrogen containing metal powder according to claim 7 , wherein said reducing agent and said metal salt are each added either continuously or in portions to said diluent salt.
12. A porous sintered body produced by sintering a nitrogen containing metal powder according to claim 1 .
13. A porous sintered body produced by sintering a nitrogen containing metal powder according to claim 3 .
14. A solid electrolytic capacitor equipped with an anode electrode formed from a porous sintered body according to claim 12 .
15. A solid electrolytic capacitor equipped with an anode electrode formed from a porous sintered body according to claim 13 .
16. A nitrogen containing metal powder according to claim 2 , wherein said metal is at least one metal selected from a group consisting of niobium, tantalum, and niobium-tantalum alloy.
17. A production process for a nitrogen containing metal powder according to claim 2 , in which a metal salt containing said metal is reacted with a reducing agent and undergoes reduction within a molten diluent salt, thereby generating said metal, wherein
a nitrogen containing gas is introduced into a space contacting a reaction melt comprising said metal salt, said reducing agent and said diluent salt,
thereby generating said metal and incorporating said nitrogen within said metal.
18. A porous sintered body produced by sintering a nitrogen containing metal powder according to claim 16 .
19. A porous sintered body produced by sintering a nitrogen containing metal powder according to claim 2 .
20. A solid electrolytic capacitor equipped with an anode electrode formed from a porous sintered body according to claim 19 .