Inkjet printing recording material
A novel recording material for the inkjet printing process has a substrate and an ink receiving layer which is applied on at least one side of the substrate, the ink receiving layer containing an inorganic pigment and an ink fixative comprising at least two substances. The first substance is a polyamine epichorohydrin and the second substance is a polyvalent metal salt. This recording material is characterized in that the first substance is a medium-molecular, branched polyamine epichlorohydrin condensation product, the ratio of the first substance to the second substance is between 3:1 and 16:1, the pigment makes up at least 80 percent by weight with a D 50 particle size (Malvern) ranging from 4 μm inclusive to 12 μm inclusive, and the ratio of ink fixative to pigment ranges from 1:2 inclusive to 1:6 inclusive. The invention is further directed to a method for recording by the discontinuous inkjet printing process which uses the novel recording material.
1. A recording material for an inkjet printing process comprising a substrate and an ink receiving layer applied on at least one side of the substrate, the ink receiving layer containing an inorganic pigment and an ink fixative comprising at least first and second substances, the first substance being a polyamine epichlorohydrin and the second substance being a polyvalent metal salt, wherein the first substance is a branched polyamine epichlorohydrin condensation product that has a viscosity in a range from 15 m Pa*s to 50 m Pa*s as a 10-percent aqueous solution as determined by using a Brookfield spindle 1 at 100 rpm and 25° C., the ratio of the first substance to the second substance is between 3:1 and 16:1, at least 80 percent by weight of the pigment is made of particles having a D 50 particle size (Malvern) ranging from 4 μm inclusive to 12 μm inclusive, and the ratio of ink fixative to pigment ranges from 1:2 inclusive to 1:6 inclusive.
2. The recording material of claim 1 , wherein the second substance is a polyvalent metal salt selected from a group including magnesium chloride, aluminum chloride and calcium chloride.
3. The recording material of claim 1 , characterized in that the ratio of the first substance to the second substance is between 6:1 and 14:1.
4. The recording material of claim 1 , wherein at least 80 percent by weight of the pigment is made of particles with a D 50 particle size (Malvern) ranging from 6 μm to 12 μm.
5. The recording material of claim 1 , wherein the pigment is selected from the group including aluminum hydroxide, silicic acid and silica gel.
6. The recording material of claim 1 , wherein the ratio of ink fixative to pigment ranges from 1:3 inclusive to 1:5.5 inclusive.
7. The recording material of claim 1 , wherein the ink receiving layer includes at least one binder selected from the group including polyvinyl alcohol, styrene-butadiene latex, polyacrylates and polymer dispersions of ethylene-vinyl acetate.
8. The recording material of claim 1 , further comprising at least one preparation layer arranged between the substrate and the ink receiving layer.
9. The recording material of claim 1 , wherein the ink receiving layer includes two layers positioned one on top of the other.
10. A method for recording using a discontinuous inkjet printing process comprising the step of applying a pigment-based recording ink using a discontinuous inkjet printing process onto a recording material according to claim 1 .