Dye composition for dyeing powder coatings
The invention relates to a powdery dye composition consisting essentially of C.I. Pigment Red 170 (C.I. No. 12475) and barium sulfate, wherein the barium sulfate is added before or during the production process of the C.I. Pigment Red 170. The inventive addition of barium sulfate enables non-homogeneities and caking to be avoided in the mixture.
1. A powder coating composition comprising a carboxylated polyester resin and a colorant composition consisting essentially of 70–90 wt. % C.I. Pigment Red 170 (C.I. No. 12475) and 10–30 wt. % barium sulfate.
2. The powder coating composition as claimed in claim 1 , wherein the colorant composition has a particle size distribution (d 50% ) of between 0.1 μm and 1.5 μm.
3. A process for preparing the powder coating composition as claimed in claim 1 , comprising the steps of adding the barium sulfate before or during the preparation of the C.I. Pigment Red 170 to form the colorant composition, homogenizing the colorant composition and mixing the colorant composition with the carboxylated polyester resin.
4. The process as claimed in claim 3 , wherein the adding step further comprises adding the barium sulfate during the synthesis of the C.I. Pigment Red 170 and/or immediately before, during and/or immediately after a finish of C.I. Pigment Red 170 crude pigment.
5. The process as claimed in claim 4 , wherein the adding step further comprises adding the barium sulfate is added after the finish of the C.I. Pigment Red 170 crude pigment but before the C.I. Pigment Red 170 crude pigment is dried.
6. The process as claimed in claim 3 , wherein the barium sulfate has a particle size distribution (d 50% ) of between 0.1 μm and 10 μm.
7. The powder coating composition as claimed in claim 1 , wherein powder coating composition further comprises a binder other than the carboxylated polyester resin.
8. The powder coating composition as claimed in claim 7 , wherein the powder coating composition includes at least one additive and wherein the binder includes a curing agent, wherein the binder is selected from the group consisting of epoxy resins, polyester resins, polyurethane resins, acrylate resins, and combinations thereof, and wherein the at least one additive is selected from the group consisting of shading dyes, surfactants, fillers, charge control agents for controlled setting of the electrostatic charge, dispersants, standardizers, waxes, defoamers, antidust agents, extenders, preservatives, rheology control additives, wetting agents, antioxidants, UV absorbers, light stabilizers, antistats, lubricants and devolatilizers.