Moldings of flame-retardant aromatic polycarbonate resin compositions
A molded article produced by injection-molding a molten form of a flame-retardant aromatic polycarbonate resin composition comprising: 100 parts by weight of an aromatic polycarbonate (A) (Mw: 17,000 to 35,000), 0.01 to 3 parts by weight of inorganic compound particles (B) (average diameter: 10 nm to 10 μm), 0.001 to 0.5 part by weight of an alkali metal salt (C) of an organic sulfonic acid, and 0.01 to 0.5 part by weight of a fluoropolymer (D), wherein the largest FL/t ratio of the molded article is 50 or more, wherein FL is a flow length of the composition in a mold and t is a thickness of the molded article, the FL/t ratios being obtained by measuring the thicknesses of the molded article at portions corresponding to flow paths (L) (from a gate to points at which the flow of the composition stops) of the composition in the mold during the molding, and calculating an integral of (dL/T′) along each (L) (dL: length of a segment of (L), t′: thickness of the molded article at a portion corresponding to the segment), wherein the calculated integrals are defined as the FL/t ratios.
1. A molded article of a flame-retardant aromatic polycarbonate resin composition, which is produced by injection-molding a molten form of a flame-retardant aromatic polycarbonate resin composition in a mold having at least one gate for introduction of said resin composition, said flame-retardant aromatic polycarbonate resin composition comprising:
100 parts by weight of an aromatic polycarbonate (A) having a weight average molecular weight of from 17,000 to 35,000,
0.01 to 3 parts by weight of inorganic compound particles (B) having an average particle diameter of from 10 nm to 10 μm,
0.001 to 0.5 part by weight of an alkali metal salt (C) of an organic sulfonic acid, and
0.01 to 0.5 part by weight of a fluoropolymer (D) wherein the largest value of FL/t ratios of the molded article is 50 or more, wherein FL represents a flow length of said resin composition in the mold and t represents a thickness of said molded article,
said FL/t ratios being obtained by a method comprising:
measuring the thicknesses of the molded article at portions thereof which, respectively, correspond to flow paths (L) of said molten form of the resin composition in said mold during the injection molding, said flow paths (L) extending from said gate of the mold to points in the mold at which the flow of said molten form of the resin composition stops, and
calculating an integral of (dL/t′) along each of said flow paths (L), wherein dL represents the length of a segment of flow path (L) and t′ represents the thickness of the molded article at a portion thereof which corresponds to said segment,
wherein the integrals respectively calculated with respect to said flow paths (L) are defined as the FL/t ratios of the molded article.
2. The molded article according to claim 1 , which has at least one thin portion having a thickness of 2.0 mm or less, wherein the amount of said at least one thin portion is 50% by weight or more, based on the weight of said molded article.
3. The molded article according to claim 1 , wherein said inorganic compound particles (B) are metal oxide particles.
4. The molded article according to claim 3 , wherein said metal oxide particles are silicon oxide particles produced by the dry method.
5. The molded article according to any one of claims 1 to 4 , wherein the surfaces of said inorganic compound particles (B) are modified with a silicon compound.
6. The molded article according to any one of claims 1 to 4 , wherein when said alkali metal salt (C) of an organic sulfonic acid is subjected to thermogravimetric analysis at a temperature elevation rate of 10° C./min in a nitrogen atmosphere, the temperature at which the weight reduction of said alkali metal salt (C) reaches 5% by weight is 400° C. or higher.
7. The molded article according to any one of claims 1 to 4 , which has at least one functional portion selected from the group consisting of a boss, a rib, a pin and a corner.
8. A method for producing a molded article, which comprises:
(1) charging a molten form of a flame-retardant aromatic polycarbonate resin composition into a mold by using an injection-molding machine, said flame-retardant aromatic polycarbonate resin composition comprising:
100 parts by weight of an aromatic polycarbonate (A) having a weight average molecular weight of from 17,000 to 35,000,
0.01 to 3 parts by weight of inorganic compound particles (B) having an average particle diameter of from 10 nm to 10 μm,
0.001 to 0.5 part by weight of an alkali metal salt (C) of an organic sulfonic acid, and
0.01 to 0.5 part by weight of a fluoropolymer (D),
wherein the temperature (T M :° C.) of said molten form of the resin composition charged into the mold satisfies the following formula (1):
0.005 Mw+ 175≦ T M ≦350 (1)
wherein Mw represents the weight average molecular weight of said aromatic polycarbonate (A),
(2) cooling said resin composition in the mold to thereby form a molded article in the mold, and
(3) recovering said molded article from the mold.
9. The method according to claim 8 , wherein said inorganic compound particles (B) are metal oxide particles.
10. The method according to claim 9 , wherein said metal oxide particles are silicon oxide particles produced by the dry method.
11. The method according to any one of claims 8 to 10 , wherein the surfaces of said inorganic compound particles (B) are modified with a silicon compound.
12. The method according to any one of claims 8 to 10 , wherein when said alkali metal salt (C) of an organic sulfonic acid is subjected to thermogravimetric analysis at a temperature elevation rate of 10° C./min in a nitrogen atmosphere, the temperature at which the weight reduction of said alkali metal salt (C) reaches 5% by weight is 400° C. or higher.
13. The method according to any one of claims 8 to 10 , wherein said molded article has at least one functional portion selected from the group consisting of a boss, a rib, a pin and a corner.