Hydrogenated copolymer and composition thereof
A hydrogenated copolymer obtained by hydrogenating an unhydrogenated copolymer comprising conjugated diene monomer units and vinyl aromatic monomer units, the hydrogenated copolymer containing at least one hydrogenated copolymer block (B) which is obtained by hydrogenating an unhydrogenated random copolymer block comprised of conjugated diene monomer units and vinyl aromatic monomer units, wherein the hydrogenated copolymer has the following characteristics: the hydrogenated copolymer has a content of the vinyl aromatic monomer units of from more than 40% by weight to less than 95% by weight; at least one peak of loss tangent (tan δ) is observed at −10 to 80° C. in a dynamic viscoelastic spectrum obtained with respect to the hydrogenated copolymer; and substantially no crystallization peak ascribed to the copolymer block (B) is observed at −20 to 80° C. in a differential scanning calorimetry (DSC) chart obtained with respect to the hydrogenated copolymer.
1. A hydrogenated copolymer obtained by hydrogenating an unhydrogenated copolymer comprising conjugated diene monomer units and vinyl aromatic monomer units, said hydrogenated copolymer comprising:
at least two polymer blocks (A) of vinyl aromatic monomer units, and
at least one hydrogenated copolymer block (B) which is obtained by hydrogenating an unhydrogenated random copolymer block comprised of conjugated diene monomer units and vinyl aromatic monomer units, said unhydrogenated random copolymer block having a vinyl bond content of 60% or less as measured with respect to the conjugated diene monomer units in said unhydrogenated random copolymer block,
said hydrogenated copolymer having the following characteristics (1) to (6):
(1) said hydrogenated copolymer has a content of said vinyl aromatic monomer units of from more than 50% by weight to less than 95% by weight, based on the weight of said hydrogenated copolymer,
(2) said hydrogenated copolymer has a content of said at least two polymer blocks (A) of 5 to 60% by weight, based on the weight of said hydrogenated copolymer,
(3) said hydrogenated copolymer has a weight average molecular weight of from 30,000 to 1,000,000,
(4) said hydrogenated copolymer has a hydrogenation ratio of 75% or more, as measured with respect to the double bonds in said conjugated diene monomer units,
(5) at least one peak of loss tangent (tan δ) is observed at −10 to 80° C. in a dynamic viscoelastic spectrum obtained with respect to said hydrogenated copolymer, and
(6) substantially no crystallization peak ascribed to said at least one hydrogenated copolymer block (B) is observed at −20 to 80° C. in a differential scanning calorimetry (DSC) chart obtained with respect to said hydrogenated copolymer.
2. The hydrogenated copolymer according to claim 1 , which is a foam.
3. The hydrogenated copolymer according to claim 1 , which is a building material, a vibration damping, soundproofing material or an electric wire coating material.
4. A hydrogenated copolymer composition comprising:
1 to 99 parts by weight, relative to 100 parts by weight of the total of components (a-0) and (b), of (a-0) the hydrogenated copolymer of claim 1 , and
99 to 1 part by weight, relative to 100 parts by weight of the total of components (a-0) and (b), of (b) at least one polymer selected from the group consisting of a thermoplastic resin other than the hydrogenated copolymer (a-0) and a rubbery polymer other than the hydrogenated copolymer (a-0).
5. The hydrogenated copolymer composition according to claim 4 , which is a foam.
6. The hydrogenated copolymer composition according to claim 4 , which is a building material, a vibration damping, soundproofing material or an electric wire coating material.
7. A crosslinked hydrogenated copolymer composition obtained by subjecting the hydrogenated copolymer composition of claim 4 to a crosslinking reaction in the presence of a crosslinking agent.
8. A crosslinked hydrogenated copolymer obtained by subjecting an uncrosslinked hydrogenated copolymer to a crosslinking reaction in the presence of a crosslinking agent,
said uncrosslinked hydrogenated copolymer comprising:
at least two polymer blocks (A) of vinyl aromatic monomer units and
at least one hydrogenated copolymer block (B) which is obtained by hydrogenating an unhydrogenated random copolymer block comprised of conjugated diene monomer units and vinyl aromatic monomer units, said unhydrogenated random copolymer block having a vinyl bond content of 60% or less as measured with respect to the conjugated diene monomer units in said unhydrogenated random copolymer block,
wherein said uncrosslinked hydrogenated copolymer has the following characteristics (1) to (6):
(1) said uncrosslinked hydrogenated copolymer has a content of said vinyl aromatic monomer units of from more than 40% by weight to less than 95% by weight, based on the weight of said uncrosslinked hydrogenated copolymer,
(2) said uncrosslinked hydrogenated copolymer has a content of said at least two polymer blocks (A) of from greater than 0% by weight up to 60% by weight, based on the weight of said uncrosslinked hydrogenated copolymer,
(3) said uncrosslinked hydrogenated copolymer has a weight average molecular weight of from 30,000 to 1,000,000,
(4) said uncrosslinked hydrogenated copolymer has a hydrogenation ratio of 75% or more, as measured with respect to the double bonds in said conjugated diene monomer units,
(5) at least one peak of loss tangent (tan d) is observed at −10 to 80° C. in a dynamic viscoelastic spectrum obtained with respect to said uncrosslinked hydrogenated copolymer, and
(6) substantially no crystallization peak ascribed to said at least one hydrogenated copolymer block (B) is observed at −20 to 80° C. in a differential scanning calorimetry (DSC) chart obtained with respect to said uncrosslinked hydrogenated copolymer.
9. An adhesive composition comprising:
100 parts by weight of a hydrogenated copolymer and
20 to 400 parts by weight of a tackifier, said hydrogenated copolymer comprising
at least two polymer blocks (A) of vinyl aromatic monomer units and
at least one hydrogenated copolymer block (B) which is obtained by hydrogenating an unhydrogenated random copolymer block comprised of conjugated diene monomer units and vinyl aromatic monomer units, said unhydrogenated random copolymer block having a vinyl bond content of 60% or less as measured with respect to the conjugated diene monomer units in said unhydrogenated random copolymer block,
wherein said hydrogenated copolymer has the following characteristics (1) to (6):
(1) said hydrogenated copolymer has a content of said vinyl aromatic monomer units of from more than 40% by weight to less than 95% by weight, based on the weight of said hydrogenated copolymer,
(2) said hydrogenated copolymer has a content of said at least two polymer blocks (A) of from greater than 0% by weight to 60% by weight, based on the weight of said hydrogenated copolymer,
(3) said hydrogenated copolymer has a weight average molecular weight of from 30,000 to 1,000,000,
(4) said hydrogenated copolymer has a hydrogenation ratio of 75% or more, as measured with respect to the double bonds in said conjugated diene monomer units,
(5) at least one peak of loss tangent (tan d) is observed at −10 to 80° C. in a dynamic viscoelastic spectrum obtained with respect to said hydrogenated copolymer, and
(6) substantially no crystallization peak ascribed to said at least one hydrogenated copolymer block (B) is observed at −20 to 80° C. in a differential scanning calorimetry (DSC) chart obtained with respect to said hydrogenated copolymer.
10. An asphalt composition comprising:
0.5 to 50 parts by weight of a hydrogenated copolymer and
100 parts by weight of an asphalt,
said hydrogenated copolymer comprising:
at least two polymer blocks (A) of vinyl aromatic monomer units and
at least one hydrogenated copolymer block (B) which is obtained by hydrogenating an unhydrogenated random copolymer block comprised of conjugated diene monomer units and vinyl aromatic monomer units, said unhydrogenated random copolymer block having a vinyl bond content of 60% or less as measured with respect to the conjugated diene monomer units in said unhydrogenated random copolymer block,
wherein said hydrogenated copolymer has the following characteristics (1) to (6):
(1) said hydrogenated copolymer has a content of said vinyl aromatic monomer units of from more than 40% by weight to less than 95% by weight, based on the weight of said hydrogenated copolymer,
(2) said hydrogenated copolymer has a content of said at least two polymer blocks (A) of from greater than 0% by weight to 60% by weight, based on the weight of said hydrogenated copolymer,
(3) said hydrogenated copolymer has a weight average molecular weight of from 30,000 to 1,000,000,
(4) said hydrogenated copolymer has a hydrogenation ratio of 75% or more, as measured with respect to the double bonds in said conjugated diene monomer units,
(5) at least one peak of loss tangent (tan d) is observed at −10 to 80° C. in a dynamic viscoelastic spectrum obtained with respect to said hydrogenated copolymer, and
(6) substantially no crystallization peak ascribed to said at least one hydrogenated copolymer block (B) is observed at −20 to 80° C. in a differential scanning calorimetry (DSC) chart obtained with respect to said hydrogenated copolymer.