Highly filled elastomeric resin compositions with added microsilica for processability
The present invention relates to elastomeric compounds having a high filler content additionally containing 1 to 400% by weight of resin of microsilica as a modifier to improve the processability. Thereafter, the invention relates to a method for production of elastomeric compounds having a high filler content, wherein microsilica is added to the elastomeric compounds in an amount of 1 to 400% by weight of resin as a modifier to improve processability.
1. A method for production of a highly filled elastomeric compound comprising:
forming a highly filled elastomeric compound from an elastomeric resin wherein a filler comprises about 110% to about 500% by weight of the elastomeric resin; and
adding dry microsilica to the highly filled elastomeric compound in an amount of 255% to 400% by weight of elastomeric resin as a modifier to improve processability, wherein the microsilica is particulate amorphous SiO 2 obtained from a process in which silica is reduced to SiO-gas and oxidized in vapor phase to form amorphous silica which contains at least 70% by weight silica (SiO 2 ) and has a specific density of 2.1-2.3 g/cm 3 and a surface area of 15-40 m 2 /g, and has primary particles being substantially spherical with an average size of about 0.15 μm;
wherein the elastomeric resin comprises a polymer selected from the group consisting of natural rubber (NR), ethylene-propylene-diene rubber (EPM and EPDM), styrene-butadiene rubber (SBR), acrylonitrile-butadiene rubber (NBR), polychloroprene rubber (PCP), acrylate rubber, NBR blended with polyvinyl chloride, ethylene vinyl acetate copolymer and blends thereof.
2. The method according to claim 1 , wherein microsilica is added to the highly filled elastomeric compound in an amount of 20% to 300% by weight of elastomeric resin.
3. The method for production of a highly filled elastomeric compound of claim 1 wherein the elastomeric resin consists of a polymer selected from the group consisting of natural rubber (NR), ethylene-propylene-diene rubber (EPM and EPDM), styrene-butadiene rubber (SBR), acrylonitrile-butadiene rubber (NBR), polychloroprene rubber (PCP), acrylate rubber, ethylene vinyl acetate copolymer and blends thereof.
4. A method of using dry microsilica as a modifier to improve processability of a highly filled elastomeric compound having a filler content of about 110% to about 500% by weight of elastomeric resin, comprising a step of adding 255% to 400% by weight of elastomeric resin of microsilica to said compound, wherein the microsilica is particulate amorphous SiO 2 obtained from a process in which silica is reduced to SiO-gas and oxidized in vapor phase to form amorphous silica, which contains at least 70% by weight silica (SiO 2 ) and has a specific density of 2.1-2.3 g/cm 3 and a surface area of 15-40 m 2 /g, and has primary particles being substantially spherical with an average size of about 0.15 μm;
wherein the elastomeric resin comprises a polymer selected from the group consisting of natural rubber (NR), ethylene-propylene-diene rubber (EPM and EPDM), styrene-butadiene rubber (SBR), acrylonitrile-butadiene rubber (NBR), polychloroprene rubber (PCP), acrylate rubber, NBR blended with polyvinyl chloride, ethylene vinyl acetate copolymer and blends thereof.
5. The method of using microsilica as a modifier to improve processability of a highly filled elastomeric compound of claim 4 , wherein the elastomeric resin consists of a polymer selected from the group consisting of natural rubber (NR), ethylene-propylene-diene rubber (EPM and EPDM), styrene-butadiene rubber (SBR), acrylonitrile-butadiene rubber (NBR), polychloroprene rubber (PCP), acrylate rubber, ethylene vinyl acetate copolymer and blends thereof.