Methods for manufacturing ceramic parts using microwave sintering
A method for manufacturing ceramic parts with a certain porosity by sintering using microwaves, the materials to be sintered being arranged in a vessel, wherein the microwaves introduce sintering energy into the materials to be sintered via electromagnetic waves in the range of vacuum wavelengths between 5 cm-20 cm in multimode having an electromagnetic power of up to one kilowatt, and besides being built from primary materials for the structure of the vessel, the vessel is built from a secondary material which comprises, in particular, a mixture of or mixed crystals of non-metallic, para-, ferro- or antiferromagnetic materials.
1. Method for manufacturing ceramic parts with a certain porosity by sintering using microwaves, the materials to be sintered being arranged in a vessel, said method comprising:
assembling a bottom element, an intermediate element, and a top element to define a receiving portion, the bottom, intermediate, and top elements being formed from a primary material;
introducing a secondary material into an annular recess of the intermediate element so that the secondary material is surrounded by the primary material, the annular recess surrounding the receiving portion, wherein the secondary material comprises at least one material selected from the group consisting of: non-metallic materials, para-magnetic materials, ferro-magnetic materials and antiferromagnetic materials;
introducing the materials to be sintered into the receiving portion; and
introducing microwave sintering energy into the materials to be sintered via electromagnetic waves in the range of vacuum wavelengths between 5 cm-20 cm in multimode having an electromagnetic power of up to one kilowatt.
2. Method of claim 1 , wherein introducing the secondary material into the annular recess comprises introducing a secondary material element into the annular recess.
3. Method of claim 1 , wherein said wavelength range of the electromagnetic waves is between 11-13 cm.
4. Method of claim 1 , wherein said ceramic parts have a porosity of between 0-50 percent by volume.
5. Method of claim 4 , wherein said porosity is between 10-30% by volume.
6. Method of claim 1 , wherein said ceramic parts are infiltrated with a glass material to produce the final strength.
7. Method of claim 1 , wherein said ceramic parts are sintered to a defined final density of at least 80% of the theoretical density of the respective material.
8. Method of claim 1 , wherein said ceramic parts are dental restorations.
9. Method of claim 8 , wherein said dental restorations are veneered using a glass material.
10. Method of claim 1 , wherein said material is selected from the group consisting of: Al 2 O 3 , Spinell, Ce- or Y-stabilized ZrO 2 , and mixtures thereof.