Nickel based compound positive electrode material primary cell
According to the invention, a high capacity alkali primary battery excellent in high rate characteristics is obtained using a positive electrode active substance, wherein the particles of the nickel oxyhydroxide base compound as the positive electrode active substance has a surface coated with a higher oxide of cobalt and comprises zinc and cobalt separately or an eutectic crystal with zinc and cobalt, and a half-width of an X-ray diffraction peak at a diffraction angle at around 18° in an X-ray diffraction pattern of 0.4 to 0.48 obtained by using a CuKα line as an X-ray source. A further excellent battery is obtained by using zinc containing a powder with a particle diameter of 75 μm or less in the range of 10% by mass or more and 20% by mass or less.
1 . A primary battery comprising a positive electrode material of a nickel base compound using particles of a nickel oxyhydroxide base compound as a positive electrode active substance,
the particles of the nickel oxyhydroxide base compound having a surface coated with a higher oxide of cobalt and comprising zinc and cobalt separately or an eutectic crystal with zinc and cobalt,
the particles of the nickel oxyhydroxide compound having a half-width of an X-ray diffraction peak in an X-ray diffraction pattern of 0.4 to 0.48 obtained by using a CuKα line as an X-ray source.
2 . The primary battery comprising the positive electrode material of the nickel base compound according to claim 1 , wherein the content of the cobalt higher oxide compound coated on the surface of the positive electrode active substance is 0.5% by mass or more and 20% by mass or less.
3 . A primary battery comprising a positive electrode material of a nickel base compound using particles of a nickel oxyhydroxide base compound as a positive electrode active substance and zinc or an alloy of zinc as a negative electrode material,
the particles of the nickel oxyhydroxide base compound having a surface coated with a higher oxide of cobalt and comprising zinc and cobalt separately or an eutectic crystal with zinc and cobalt,
the particles of the nickel oxyhydroxide base compound having a half-width of an X-ray diffraction peak in an X-ray diffraction pattern of 0.4 to 0.48 obtained by using a CuKα line as an X-ray source,
the zinc or an alloy of zinc as the negative electrode material comprising a powder with a particle diameter of 75 μm or less in the range of 10% by mass or more and 20% by mass or less.
4 . The primary battery comprising the positive electrode material of the nickel base compound according to claim 3 , wherein zinc or an alloy of zinc as the negative electrode material comprises a powder with a particle diameter of 75 μm or less in the range of 10% by mass or more and 20% by mass or less.