Polyurethane dispersion and articles prepared therefrom
The present invention is to a polyurethane dispersion and products produced therefrom wherein the dispersion contains a polyurethane prepolymer produced from the a reaction of an excess of a polyisocyanate with an isocyanate reactive molecule wherein the polyisocyanate is a bis(isocyanatomethyl)cyclohexane. Preferably the isocyanate comprises (i) trans-1,4-bis(isocyanatomethyl)cyclohexane or (ii) an isomeric mixture of two or more of cis-1,3-bis(isocyanatomethyl)cyclohexane, trans-1,3-bis(isocyanatomethyl)cyclohexane, cis-1,4-bis(isocyanatomethyl)cyclohexane and trans-1,4-bis(isocyanatomethyl)cyclohexane, with the proviso said isomeric mixture comprises at least about 5 weight percent of said trans-1,4-bis(isocyanatomethyl)cyclohexane.
1. An aqueous polyurethane dispersion consisting of a polyurethane prepolymer produced from the reaction of an excess of a polyisocyanate and a molecule having hydrogen active moieties, optionally a chain extender, and optionally a surfactant, wherein the polyisocyanate consists of (i) trans-1,4-bis(isocyanatomethyl)cyclohexane or (ii) an isomeric mixture of two or more of cis-1,3-bis(isocyanatomethyl)cyclohexane, trans-1,3-bis(isocyanatomethyl)cyclohexane, cis-1,4-bis(isocyanatomethyl)cyclohexane and trans-1,4-bis(isocyanatomethyl)cyclohexane, with the proviso said isomeric mixture consists of at least about 5 weight percent of said trans-1,4-bis(isocyanatomethyl)cyclohexane, wherein the dispersion further consists of from about 0.01 to about 0.5 parts organometallic compounds per 100 parts polyurethane prepolymer, by weight.
2. The dispersion of claim 1 wherein the molecule having hydrogen active moieties is a polyol or polyol blend having a weight average molecular weight of 300 to 10,000 and an average functionality of 1.8 to 4.5.
3. The dispersion of claim 2 wherein the polyol is an aliphatic or aromatic polyol selected from a polyester, a polyether, polylactone, polyolefin, polycarbonate or a blend thereof.
4. The dispersion of claim 1 wherein the dispersion contains a polyamine chain extender.
5. The dispersion of claim 4 wherein the chain extender is selected from piperazine, ethylenediamine or bis(aminomethyl)cyclohexane.
6. The dispersion of claim 1 wherein the dispersion contains an anionic, ionic, cationic or zwitterionic external surfactant.
7. The dispersion of claim 1 wherein the dispersion is stabilized by means of an internal surfactant.
8. A coating, film, elastomer or microcellular foam produced from the dispersion of claim 1 .
9. A ultraviolet or light stable coating, film or elastomer produced from the dispersion of claim 1 .
10. A polyurethane dispersion consisting essentially of a polyurethane prepolymer produced from the reaction of an excess of a polyisocyanate and a polyol having a weight average molecular weight of 300 to 10,000 and an average functionality of 1.8 to 4.5, optionally a chain extender and optionally a surfactant, wherein the polyisocyanate consists essentially of a bis(isocyanatomethyl)cyclohexane compound, and wherein the polyol is an aliphatic or aromatic polyol selected from a polyester, a polyether, polyactone, polyolefin, polycarbonate or a blend thereof; wherein the dispersion further consists essentially of from about 0.01 to about 0.5 parts organometallic compounds per 100 parts polyurethane prepolymer, by weight.
11. A polyurethane dispersion comprising a polyurethane prepolymer produced from the reaction of an excess of a polyisocyanate and a molecule having hydrogen active moieties, optionally a chain extender and optionally a surfactant, wherein the polyisocyanate comprises a bis(isocyanatomethyl)cyclohexane compound, wherein the dispersion comprises 30 to 75 weight percent solids, and wherein the solids comprise particles having a mean particle size of less than about 5 microns; wherein the dispersion further comprises from about 0.01 to about 0.5 parts organometallic compounds per 100 parts polyurethane prepolymer, by weight.
12. The dispersion of claim 11 further comprising tertiary amines.
13. The dispersion of claim 11 wherein the polyurethane is dispersed in an aqueous medium.
14. The dispersion of claim 13 wherein the aqueous medium comprises less than 5 percent residual organic solvent.
15. The dispersion of claim 11 wherein the molecule having hydrogen active moieties is a polyol or polyol blend having a weight average molecular weight of 300 to 10,000 and an average functionality of 1.8 to 4.5.
16. The dispersion of claim 15 wherein the polyol is an aliphatic or aromatic polyol selected from a polyester, a polyether, polylactone, polyolefin, polycarbonate or a blend thereof.
17. The dispersion of claim 11 wherein the dispersion comprises a polyamine chain extender.
18. The dispersion of claim 17 wherein the chain extender is selected from piperazine, ethylenediamine or bis(aminomethyl)cyclohexane.
19. The dispersion of claim 11 wherein the dispersion comprises 30 to 75 weight percent solids.
20. The dispersion of claim 11 wherein the dispersion comprises an anionic, ionic, cationic or zwitterionic external surfactant.
21. The dispersion of claim 11 wherein the dispersion is stabilized by means of an internal surfactant.
22. A coating, film, elastomer or microcellular foam produced from the dispersion of claim 11 .
23. A ultraviolet or light stable coating, film or elastomer produced from the dispersion of claim 11 .
24. The dispersion of claim 11 wherein the polyisocyanate comprises 0.1 to 20 percent by weight of at least one polyisocyanate other than bis(isocyanatomethyl)cyclohexane.