Polyurethane foam dressing for wound filler and method for manufacturing thereof
A polyurethane foam dressing for a wound filler, which includes a hydrophilic polyurethane foam including a plurality of open cells with a diameter of 50 to 400 μm and a plurality of pores with a diameter of 10 to 80 μm, and a method of manufacturing the same including mixing and agitating 40 to 75 wt % pre-polymer, 15 to 45 wt % foaming agent, 5 to 35 wt % crosslinking agent, and 0.5 to 15 wt % additive containing a surfactant, a moisturizing agent, and a pigment, injecting the resulting mixture into a mold, and foaming the resulting mixture injected into the mold.
1. A hydrophilic polyurethane foam dressing comprised of a plurality of open cells and pores, characterized in that said dressing is a filling type of foam dressing which is filled into the deep wound and then used as a wound filler and has a density of 0.1 to 0.32 g/cm 3 , an absorptivity of 500 to 2000 wt %, a moisture vapor transmission rate of 2000 to 5000 g/m 2 /24 hours at 35° C. and a humidity of 90%, the average diameter of said open cells is 80 to 400 μM and the average diameter of said pores is 30 to 80 μm.
2. A method of manufacturing a hydrophilic polyurethane foam dressing comprised of a plurality of open cells and pores, including:
mixing and agitating 40 to 75 wt % polyurethane prepolymer, 15 to 45 wt % foaming agent, 5 to 35 wt % crosslinking agent, and 0.5 to 15 wt % additive containing a surfactant, a moisturizing agent, and a pigment;
injecting a resulting mixture into a mold; and
foaming the resulting mixture in the mold to produce a hydrophilic polyurethane dressing having a density of 0.1 to 0.32 g/cm 3 , an absorptivity of 500 to 2000 wt %, a moisture vapor transmission rate of 2000 to 5000 g/m 2 /24 hours at 35° C. and a humidity of 90%, the average diameter of said open cells being 80 to 400 μm and the average diameter of said pores being 30 to 80 μm.