Rounded-particle plastic powder in particular for application in laser sintering, method for production of such a powder and laser sintering process using such a powder
In a laser sintering method for producing a three-dimensional object wherein subsequent layers of the object to be formed are subsequently solidified on positions corresponding to the object, as a build-up material, a powder is used wherein the upper grain limit of the powder particles is below 100 μm, the D 0.5 -value is below 55 μm, the BET-surface is smaller than 5 m 2 /g and the grains of the powder basically have a spherical shape.
1. A polymer powder for producing a three-dimensional object by means of laser sintering, wherein the powder comprises a BET-surface which is smaller than 6 m 2 /g and at the same time the upper grain limit is below 100 μm, the D 0.9 -value is below 90 μm, and the D 0.5 -value is below 60 μm and the particles comprise a basically spherical shape.
2. A polymer powder according to claim 1 for producing a three-dimensional object by means of laser sintering, wherein the powder comprises a BET-surface which is smaller than 5 m 2 /g and at the same time the upper grain limit is below 100 μm, the D 0.9 -value is below 80 μm, and the D 0.5 -value is below 55 μm and the particles comprise a basically spherical shape.
3. A powder according to claim 1 , wherein the powder has a BET-surface having a value smaller than or equal to 4 m 2 /g.
4. A powder according to claim 3 , wherein the powder has a BET-surface having a value smaller than or equal to 3 m 2 /g.
5. A powder according to claim 4 , wherein the powder has a BET-surface having a value smaller than or equal to 2 m 2 /g.
6. A powder for manufacturing a three-dimensional object by means of laser sintering according to claim 1 , wherein a laser sintering refreshing factor is less than 50 percent.
7. A powder according to claim 6 , wherein the refreshing factor is less than 30 percent.
8. A powder according to claim 1 , wherein the powder is a polyamide powder.
9. A powder according to claim 1 , wherein the powder consists of polyamide 11 or polyamide 12.
10. A powder according to claim 8 , wherein the powder is a precipitated PA12 powder.
11. A method for producing a powder according to one of claims 1 , 2 - 10 , wherein as a base material a plastic powder attained by means of precipitation or milling is used which is mechanically or mechanically-thermally mixed for at least one minute in an appropriate aggregate.
12. A method according to claim 11 wherein the base material has at least one further powder component.
13. A method according to claim 12 wherein a further powder component is a polymer powder or an additive.
14. A method for manufacturing a three-dimensional object by means of laser sintering wherein subsequent layers of the object to be formed are subsequently solidified from solidifiable powder material in positions corresponding to the object and a powder as in any one of claims 1 or 2 - 10 is used as powder material.
15. A method according to claim 14 wherein the powder base material has at least one further powder component.
16. A method according to claim 15 wherein a further powder component is a polymer powder or an additive.