Liquid setting accelerator for a composition comprising Portland cement
The invention relates to a setting accelerator for a composition comprising Portland cement, in the form of a slurry comprising at least one calcium aluminate, 0.5 4%, preferably 0.6 2.3% of an aluminous cement setting inhibitor by weight in relation to the overall weight of the calcium alumnate, and an anti-sedimentation agent.
1. A setting accelerator for a composition comprising Portland cement, comprising:
at least one calcium aluminate;
a setting inhibitor of aluminous cements comprising boric acid and/or at least one boric acid salt, the setting inhibitor representing from 0.5 to 4% by weight relative to the total weight of the calcium aluminate; and
at least one anti-settling agent, wherein
said setting accelerator is an aqueous suspension.
2. The setting accelerator according to claim 1 , further comprising at least one dispersive agent.
3. The setting accelerator according to claim 1 , wherein,
the setting inhibitor further comprises citric acid and/or at least one citric acid salt,
the boric acid and/or the boric acid salt represents from 0.4 to 3% by weight of the total weight of the calcium aluminate, and
citric acid and/or the citric acid salt represents from 0.1 to 1% by weight of the total weight of the calcium aluminate.
4. The setting accelerator according to claim 1 , wherein the setting inhibitor consists of boric acid and/or at least one boric acid salt,
the boric acid and/or the boric acid salt(s) represents from 0.5 to 4% in weight of the total weight of the calcium aluminate.
5. The setting accelerator according to claim 3 , wherein the boric acid salt is selected from the group consisting of zinc borate, sodium borate and mixtures thereof.
6. The setting accelerator according to claim 3 , wherein the setting inhibitor comprises boric acid and citric acid.
7. The setting accelerator according to claim 2 , wherein the dispersive agent represents from 0.3 to 1.7% by weight of the total weight of the calcium aluminate.
8. The setting accelerator according to claim 1 , wherein the anti-settling agent represents from 0.2 to 0.9% by weight of the total weight of the calcium aluminate.
9. The setting accelerator according to claim 1 , wherein the anti-settling agent is selected from the group consisting of Xanthan gum, Welan gum, Bentonite and mixtures thereof.
10. The setting accelerator according to claim 1 , further comprising an anti-bacterial agent representing from 0.2 to 0.9% in weight of the total weight of the calcium aluminate.
11. The setting accelerator according to claim 1 , further comprising at least one coloring agent.
12. The setting accelerator according to claim 1 , wherein the composition comprising Portland cement is selected from the group consisting of Portland cement, slag cements, pozzolana cements and hydraulic limes, as well as among mortars and concretes comprising Portland cement, slag cement, pozzolana cement and hydraulic lime.
13. The setting accelerator according to claim 2 wherein,
the setting inhibitor further comprises citric acid and/or at least one citric acid salt,
the boric acid salt and/or the boric acid salt represents from 0.4 to 3% by weight of the total weight of the calcium aluminate, and
the citric acid and/or the citric acid salt represents from 0.1 to 1% by weight of the total weight of the calcium aluminate.
14. The setting accelerator according to claim 2 wherein,
the setting inhibitor consists of boric acid and/or at least one boric acid salt, and
the boric acid and/or the boric acid salt represents from 0.5 to 4% by weight of the total weight of the calcium aluminate.
15. The setting accelerator according to claim 3 , wherein the boric acid salt is selected from the group consisting of zinc borate, sodium borate and mixtures thereof.